Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Lubriloy Compounds Feature
- Improved impact over PTFE filled materials
- Lower mold deposits
- Excellent surface finish & colorability
- Lower S.G. vs. PTFE filled materials
- Non-halogenated lubrication
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
PA 6/6 based LUBRILOY alloys are typically used in automotive and industrial applications for gears, sliders, bearings and bushings. They feature good wear, low friction, low moisture absorption and good vibration damping characteristics.
Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield) ¹¹ 47 MPa ASTM D638 Tensile Stress (Yield) ¹¹ 43 MPa ISO 527 Tensile Stress (Break) ¹¹ 43 MPa ISO 527 Tensile Stress (Break) ¹¹ 43 MPa ASTM D638 Tensile Strain (Yield) ¹¹ 6 % ASTM D638 Tensile Strain (Yield) ¹¹ 8.8 % ISO 527 Tensile Strain (Break) ¹¹ 29.6 % ISO 527 Tensile Strain (Break) ¹¹ 38.6 % ASTM D638 Tensile Modulus (at 50 mm/min) ¹¹ 1990 MPa ASTM D638 Flexural Stress ¹¹ 69 MPa ISO 178 Flexural Stress ¹¹ 67 MPa ASTM D790 Flexural Modulus ¹¹ 2200 MPa ISO 178 Flexural Modulus ¹¹ 1930 MPa ASTM D790 Tensile Modulus (at 1 mm/min) ¹¹ 2100 MPa ISO 527 - Physical Properties
Value Units Test Method / Conditions Density ¹¹ 1.02 g/cm³ ISO 1183 Density ¹¹ 1.02 g/cm³ ASTM D792 Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ 0.3 % ASTM D570 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 2.6 % ASTM D955 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 2.57 % ISO 294 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 2.6 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 2.6 % ISO 294 Wear Factor Washer ¹¹ 12 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified: Manual Dynamic COF ¹¹ 0.31 - ASTM D3702 Modified: Manual Static COF ¹¹ 0.27 - ASTM D3702 Modified: Manual Moisture Absorption (at 23°C, 50% RH) ¹¹ 0.43 % ISO 62 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ 66 °C ASTM D648 Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 62 °C ASTM D648 Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 67 °C ISO 75/Af Relative Temperature Index (Electrical) ᵖ ¹¹ 65 °C UL 746B Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ 65 °C UL 746B Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ 65 °C UL 746B - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, at 23°C) ¹¹ No break J/m ASTM D4812 Izod Impact (Notched, at 23°C) ¹¹ 74 J/m ASTM D256 Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ 6 J ASTM D3763 Multi-Axial Impact ¹¹ 1 J ISO 6603 Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 137 kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 6 kJ/m² ISO 180/1A - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 80 °C - Drying Time ⁷ 4 Hrs - Maximum Moisture Content ⁷ 0.15 - 0.25 % - Melt Temperature ⁷ 270 - 280 °C - Front - Zone 3 Temperature ⁷ 295 - 305 °C - Middle - Zone 2 Temperature ⁷ 280 - 295 °C - Rear - Zone 1 Temperature ⁷ 265 - 275 °C - Mold Temperature ⁷ 80 - 95 °C - Back Pressure ⁷ 0.2 - 0.3 MPa - Screw Speed ⁷ 30 - 60 rpm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94HB Flame Class Rating) ᵖ 1.5 mm UL 94 - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.