Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break, 5 mm/min) ¹¹ 61 MPa ISO 527 Tensile Stress (Yield) ¹¹ 55 MPa ISO 527 Tensile Stress (Yield) ¹¹ 63 MPa ASTM D638 Tensile Strain (Break, 5 mm/min) ¹¹ 11.3 % ISO 527 Tensile Stress (Break) ¹¹ 55 MPa ISO 527 Tensile Stress (Break) ¹¹ 63 MPa ASTM D638 Tensile Modulus (at 1 mm/min) ¹¹ 2600 MPa ISO 527 Tensile Strain (Yield) ¹¹ 5.4 % ASTM D638 Tensile Strain (Yield) ¹¹ 6.7 % ISO 527 Flexural Stress (Yield, at 2 mm/min) ¹¹ 90 MPa ISO 178 Tensile Strain (Break) ¹¹ 6.2 % ASTM D638 Tensile Strain (Break) ¹¹ 7.2 % ISO 527 Flexural Modulus (at 2 mm/min) ¹¹ 2400 MPa ISO 178 Tensile Modulus (at 50 mm/min) ¹¹ 2480 MPa ASTM D638 Flexural Stress ¹¹ 84 MPa ISO 178 Flexural Stress ¹¹ 88 MPa ASTM D790 Flexural Modulus ¹¹ 2270 MPa ASTM D790 Flexural Modulus ¹¹ 2400 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ 1.8 - 2.3 % SABIC method Wear Factor Washer ¹¹ 16 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified: Manual Dynamic COF ¹¹ 0.32 - ASTM D3702 Modified: Manual Static COF ¹¹ 0.21 - ASTM D3702 Modified: Manual Density ¹¹ 1.27 g/cm³ ISO 1183 Density ¹¹ 1.27 g/cm³ ASTM D792 Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ 0.55 % ASTM D570 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 1.9 - 3.3 % ASTM D955 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 1.88 - 3.29 % ISO 294 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 1.9 - 3.3 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 1.88 - 3.29 % ISO 294 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 219 °C ISO 75/Bf Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 70 °C ISO 75/Af Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 70 °C ASTM D648 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.0000792 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.0000972 1/°C ASTM E831 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 39 kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 4 kJ/m² ISO 180/1A Izod Impact (Unnotched, at 23°C) ¹¹ 571 J/m ASTM D4812 Izod Impact (Notched, at 23°C) ¹¹ 42 J/m ASTM D256 Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ 3 J ASTM D3763 - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 80 °C - Drying Time ⁷ 4 Hrs - Maximum Moisture Content ⁷ 0.15 - 0.25 % - Melt Temperature ⁷ 275 - 290 °C - Front - Zone 3 Temperature ⁷ 295 - 305 °C - Middle - Zone 2 Temperature ⁷ 280 - 295 °C - Rear - Zone 1 Temperature ⁷ 265 - 275 °C - Mold Temperature ⁷ 80 - 95 °C - Back Pressure ⁷ 0.2 - 0.3 MPa - Screw Speed ⁷ 30 - 60 rpm - - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.