Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break, 5 mm/min) ¹¹ 173 MPa ISO 527 Tensile Strain (Break, 5 mm/min) ¹¹ 3 % ISO 527 Tensile Modulus (at 1 mm/min) ¹¹ 9700 MPa ISO 527 Flexural Stress (Break, 2 mm/min) ¹¹ 238 MPa ISO 178 Flexural Modulus (at 2 mm/min) ¹¹ 7900 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ 0.2 - 0.4 % SABIC method Density ¹¹ 1.49 g/cm³ ISO 1183 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 261 °C ISO 75/Bf Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 249 °C ISO 75/Af - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 70 kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 13 kJ/m² ISO 180/1A - Injection Molding
Value Units Test Method / Conditions Drying Time ⁷ 4 Hrs - Drying Temperature ⁷ 80 °C - Melt Temperature ⁷ 280 - 305 °C - Rear - Zone 1 Temperature ⁷ 265 - 275 °C - Middle - Zone 2 Temperature ⁷ 280 - 295 °C - Front - Zone 3 Temperature ⁷ 295 - 305 °C - Maximum Moisture Content ⁷ 0.15 - 0.25 % - Back Pressure ⁷ 0.2 - 0.3 MPa - Screw Speed ⁷ 30 - 60 rpm - Mold Temperature ⁷ 95 - 110 °C - - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.