Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield) ¹¹ 155 MPa ISO 527 Tensile Stress (Yield) ¹¹ 157 MPa ASTM D638 Tensile Stress (Break) ¹¹ 157 MPa ASTM D638 Tensile Stress (Break) ¹¹ 155 MPa ISO 527 Tensile Strain (Yield) ¹¹ 3.3 % ASTM D638 Tensile Strain (Yield) ¹¹ 3.2 % ISO 527 Tensile Strain (Break) ¹¹ 3.3 % ASTM D638 Tensile Strain (Break) ¹¹ 3.2 % ISO 527 Tensile Modulus (at 1 mm/min) ¹¹ 8060 MPa ISO 527 Flexural Stress ¹¹ 223 MPa ISO 178 Flexural Stress ¹¹ 220 MPa ASTM D790 Flexural Modulus ¹¹ 7000 MPa ISO 178 Flexural Modulus ¹¹ 6890 MPa ASTM D790 Tensile Modulus (at 50 mm/min) ¹¹ 8270 MPa ASTM D638 - Physical Properties
Value Units Test Method / Conditions Density ¹¹ 1.42 g/cm³ ASTM D792 Density ¹¹ 1.42 g/cm³ ISO 1183 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 1.3 % ISO 294 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 1.3 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 1.9 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 1.9 % ISO 294 Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ 0.5 % ASTM D570 Wear Factor Washer ¹¹ 10 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified: Manual Dynamic COF ¹¹ 0.6 - ASTM D3702 Modified: Manual Static COF ¹¹ 0.6 - ASTM D3702 Modified: Manual - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 262 °C ISO 75/Bf Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 250 °C ISO 75/Af Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.000036 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.000036 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.000071 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 7.20E-05 1/°C ASTM E831 Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ 262 °C ASTM D648 Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 252 °C ASTM D648 Relative Temperature Index (Electrical) ᵖ ¹¹ 120 °C UL 746B Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ 65 °C UL 746B Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ 65 °C UL 746B - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 11 kJ/m² ISO 180/1A Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 67 kJ/m² ISO 180/1U Multi-Axial Impact ¹¹ 4 J ISO 6603 Izod Impact (Notched, at 23°C) ¹¹ 106 J/m ASTM D256 Izod Impact (Unnotched, at 23°C) ¹¹ 1174 J/m ASTM D4812 Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ 10 J ASTM D3763 - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 80 °C - Drying Time ⁷ 4 Hrs - Maximum Moisture Content ⁷ 0.15 - 0.25 % - Melt Temperature ⁷ 280 - 305 °C - Front - Zone 3 Temperature ⁷ 295 - 305 °C - Middle - Zone 2 Temperature ⁷ 280 - 295 °C - Rear - Zone 1 Temperature ⁷ 265 - 275 °C - Mold Temperature ⁷ 95 - 110 °C - Back Pressure ⁷ 0.2 - 0.3 MPa - Screw Speed ⁷ 30 - 60 rpm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94HB Flame Class Rating) ᵖ min. 0.75 mm UL 94 - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.