Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, 5 mm/min) ¹¹ 188 MPa ISO 527 Tensile Stress (Break, 5 mm/min) ¹¹ 185 MPa ISO 527 Tensile Strain (Yield, 5 mm/min) ¹¹ 2.8 % ISO 527 Tensile Strain (Break, 5 mm/min) ¹¹ 2.7 % ISO 527 Flexural Modulus (at 2 mm/min) ¹¹ 8980 MPa ISO 178 Tensile Modulus (at 1 mm/min) ¹¹ 10630 MPa ISO 527 Tensile Stress (Break, Type I, 5 mm/min) ¹¹ 189 MPa ASTM D638 Tensile Strain (Break, Type I, 5 mm/min) ¹¹ 2.7 % ASTM D638 Tensile Modulus (at 5 mm/min) ¹¹ 11020 MPa ASTM D638 Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ 263 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ 8920 MPa ASTM D790 - Physical Properties
Value Units Test Method / Conditions Density ¹¹ 1.4 g/cm³ ISO 1183 Density ¹¹ 1.43 g/cm³ ASTM D792 Moisture Absorption (at 23°C, 50% RH) ¹¹ 0.88 % ISO 62 Specific Gravity ¹¹ 1.4 - ASTM D792 Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ 0.57 % ASTM D570 Wear Factor Washer ¹¹ 16 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified: Manual Wear Factor Ring ¹¹ 0 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified: Manual Dynamic COF ¹¹ 0.62 - ASTM D3702 Modified: Manual Static COF ¹¹ 0.53 - ASTM D3702 Modified: Manual - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 251 °C ISO 75/Af Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 262 °C ISO 75/Bf Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ 259 °C ASTM D648 Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 249 °C ASTM D648 Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ 0.00004 1/°C ASTM D696 Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹ 0.000092 1/°C ASTM D696 Relative Temperature Index (Electrical) ᵖ ¹¹ 65 °C UL 746B Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ 65 °C UL 746B Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ 65 °C UL 746B - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 10 kJ/m² ISO 180/1A Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 62 kJ/m² ISO 180/1U Multi-Axial Impact ¹¹ 2 J ISO 6603 Izod Impact (Unnotched, at 23°C) ¹¹ 1070 J/m ASTM D4812 Izod Impact (Notched, at 23°C) ¹¹ 110 J/m ASTM D256 Instrumented Dart Impact Total Energy (at 23°C) ¹¹ 9 J ASTM D3763 - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 80 °C - Drying Time ⁷ 4 Hrs - Maximum Moisture Content ⁷ 0.15 - 0.25 % - Melt Temperature ⁷ 280 - 305 °C - Front - Zone 3 Temperature ⁷ 295 - 305 °C - Middle - Zone 2 Temperature ⁷ 280 - 295 °C - Rear - Zone 1 Temperature ⁷ 265 - 275 °C - Mold Temperature ⁷ 95 - 110 °C - Back Pressure ⁷ 0.2 - 0.3 MPa - Screw Speed ⁷ 30 - 60 rpm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94HB Flame Class Rating) ᵖ 1.5 mm UL 94 - Note
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.