Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break) ¹¹ 144 MPa ASTM D638 Tensile Stress (Break) ¹¹ 146 MPa ISO 527 Tensile Strain (Break) ¹¹ 1.8 % ISO 527 Tensile Strain (Break) ¹¹ 1.8 % ASTM D638 Tensile Modulus (at 50 mm/min) ¹¹ 13100 MPa ASTM D638 Flexural Stress ¹¹ 200 MPa ASTM D790 Flexural Stress ¹¹ 208 MPa ISO 178 Flexural Modulus ¹¹ 10960 MPa ASTM D790 Flexural Modulus ¹¹ 11440 MPa ISO 178 Tensile Modulus (at 1 mm/min) ¹¹ 12180 MPa ISO 527 - Physical Properties
Value Units Test Method / Conditions Density ¹¹ 1.69 g/cm³ ASTM D792 Density ¹¹ 1.69E+00 g/cm³ ISO 1183 Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ 0.01 % ASTM D570 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 0.1 % ASTM D955 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 0.09 % ISO 294 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 0.5 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 0.53 % ISO 294 Wear Factor Washer ¹¹ 59 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified: Manual Dynamic COF ¹¹ 0.43 - ASTM D3702 Modified: Manual Static COF ¹¹ 0.34 - ASTM D3702 Modified: Manual - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 263 °C ASTM D648 Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 260 °C ISO 75/Af - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, at 23°C) ¹¹ 528 J/m ASTM D4812 Izod Impact (Notched, at 23°C) ¹¹ 85 J/m ASTM D256 Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ 7 J ASTM D3763 Multi-Axial Impact ¹¹ 3 J ISO 6603 Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 38 kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 9 kJ/m² ISO 180/1A - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 120 - 150 °C - Drying Time ⁷ 4 Hrs - Melt Temperature ⁷ 315 - 320 °C - Front - Zone 3 Temperature ⁷ 330 - 345 °C - Middle - Zone 2 Temperature ⁷ 320 - 330 °C - Rear - Zone 1 Temperature ⁷ 305 - 315 °C - Mold Temperature ⁷ 140 - 165 °C - Back Pressure ⁷ 0.2 - 0.3 MPa - Screw Speed ⁷ 30 - 60 rpm - - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.