Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Resins and Compounds for Water Management Applications
SABIC’S specialty resins and compounds offer the water management industry design flexibility to produce products with longer lives and higher quality. Our materials are excellent candidates to replace metal and can provide weight reduction, corrosion resistance, high strength and stiffness or inherent lubricity depending on the application’s requirements.
- Internally lubricated
- Low Wear in Aqueous Environments
- Low coefficient of Friction
In addition to mechanical requirements, applications for the water management industry need certification for potable water compliance according to national standards. SABIC has developed a dedicated potable water certified portfolio to help our customers accelerate their application development time to market.
SABIC Offerings Certified for Water Management Applications:
For applications that do not require potable water certification, SABIC’s Specialties portfolio includes a wide range of specialized thermoplastic compounds based on different base resins and fillers.
Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break, 5 mm/min) ¹¹ 124 MPa ISO 527 Tensile Stress (Break) ¹¹ 124 MPa ISO 527 Tensile Stress (Break) ¹¹ 144 MPa ASTM D638 Tensile Strain (Break, 5 mm/min) ¹¹ 1.4 % ISO 527 Tensile Strain (Break) ¹¹ 1.7 % ASTM D638 Tensile Strain (Break) ¹¹ 1.4 % ISO 527 Tensile Modulus (at 1 mm/min) ¹¹ 11100 MPa ISO 527 Tensile Modulus (at 50 mm/min) ¹¹ 12340 MPa ASTM D638 Flexural Stress (Yield, at 2 mm/min) ¹¹ 216 MPa ISO 178 Flexural Stress ¹¹ 197 MPa ISO 178 Flexural Stress ¹¹ 199 MPa ASTM D790 Flexural Modulus ¹¹ 11030 MPa ASTM D790 Flexural Modulus ¹¹ 10950 MPa ISO 178 Flexural Strain (Break, at 2 mm/min) ¹¹ 2.4 % ISO 178 Flexural Modulus (at 2 mm/min) ¹¹ 9700 MPa ISO 178 Flexural Strain (Break, at 2 mm/min, 80°C) ¹¹ 2.6 % ISO 178 Flexural Strain (Break, at 2 mm/min, 120°C) ¹¹ 5.2 % ISO 178 Flexural Strain (Break, at 2 mm/min, 150°C) ¹¹ 5.8 % ISO 178 Flexural Strain (Break, at 2 mm/min, 200°C) ¹¹ 5.7 % ISO 178 Flexural Stress (Yield, at 2 mm/min, 80°C) ¹¹ 184 MPa ISO 178 Flexural Stress (Yield, at 2 mm/min, 120°C) ¹¹ 114 MPa ISO 178 Flexural Stress (Yield, at 2 mm/min, 150°C) ¹¹ 80 MPa ISO 178 Flexural Stress (Yield, at 2 mm/min, 200°C) ¹¹ 58 MPa ISO 178 Flexural Modulus (at 2 mm/min, 80°C) ¹¹ 9300 MPa ISO 178 Flexural Modulus (at 2 mm/min, 120°C) ¹¹ 4700 MPa ISO 178 Flexural Modulus (at 2 mm/min, 150°C) ¹¹ 4000 MPa ISO 178 Flexural Modulus (at 2 mm/min, 200°C) ¹¹ 3100 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Density ¹¹ 1.69 g/cm³ ASTM D792 Density ¹¹ 1.69 g/cm³ ISO 1183 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 0.1 - 0.2 % ASTM D955 Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ 0.13 - 0.18 % ISO 294 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 0.3 - 0.5 % ASTM D955 Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ 0.3 - 0.48 % ISO 294 Wear Factor Washer ¹¹ 33 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified: Manual Dynamic COF ¹¹ 0.44 - ASTM D3702 Modified: Manual Static COF ¹¹ 0.35 - ASTM D3702 Modified: Manual Moisture Absorption (at 23°C, 50% RH) ¹¹ 0.04 % ISO 62 Water Absorption (at 23°C, 24hrs) ¹¹ 0.02 % ISO 62-1 Melt Volume Rate (at 315°C, 5.0 kg) ¹¹ 10 - 15 cm³/10 min ISO 1133 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 268 °C ASTM D648 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.0000234 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.0000236 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.0000486 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ 0.0000501 1/°C ISO 11359-2 Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ 266 °C ISO 75/Af Relative Temperature Index (Electrical) ᵖ ¹¹ 200 °C UL 746B Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ 130 °C UL 746B Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ 1.30E+02 °C UL 746B Specific Heat ¹¹ 1490 J/kg-K ASTM E1269 Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ 0.000024 1/°C ISO 11359-2 Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ 130 °C UL 746B Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ 0.00005 1/°C ISO 11359-2 Thermal Conductivity ¹¹ 0.29 W/m-K ASTM D5930 - Electrical Properties
Value Units Test Method / Conditions Comparative Tracking Index (UL, PLC) ᵖ ¹¹ 4 PLC Code UL 746A Hot Wire Ignition (PLC 0) ᵖ ¹¹ min. 1.5 mm UL 746A High Ampere Arc Ignition (PLC 0) ᵖ ¹¹ min. 1.5 mm UL 746A Hot Wire Ignition (PLC 3) ᵖ ¹¹ min. 0.75 mm UL 746A High Voltage Arc Track Rate (PLC) ᵖ ¹¹ 4 PLC Code UL 746A Arc Resistance (Tungsten, PLC) ᵖ ¹¹ 7 PLC Code ASTM D495 High Ampere Arc Ignition (PLC 2) ᵖ ¹¹ min. 0.75 mm UL 746A - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, at 23°C) ¹¹ 550 J/m ASTM D4812 Izod Impact (Notched, at 23°C) ¹¹ 85 J/m ASTM D256 Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ 3 J ASTM D3763 Multi-Axial Impact ¹¹ 1 J ISO 6603 Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ 26 kJ/m² ISO 180/1U Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ 7 kJ/m² ISO 180/1A Izod Impact (Notched, 80*10*3, at -40°C) ¹¹ 8 kJ/m² ISO 180/1A Izod Impact (Unnotched, 80*10*4, at -40°C) ¹¹ 31 kJ/m² ISO 180/1U - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 120 - 150 °C - Drying Time ⁷ 4 Hrs - Melt Temperature ⁷ 315 - 320 °C - Front - Zone 3 Temperature ⁷ 330 - 345 °C - Middle - Zone 2 Temperature ⁷ 320 - 330 °C - Rear - Zone 1 Temperature ⁷ 305 - 315 °C - Mold Temperature ⁷ 140 - 165 °C - Back Pressure ⁷ 0.2 - 0.3 MPa - Screw Speed ⁷ 30 - 60 rpm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94V-0 Flame Class Rating) ᵖ min. 0.75 mm UL 94 Glow Wire Ignitability Temperature (at 0.75 mm) ᵖ 800 °C IEC 60695-2-13 Glow Wire Flammability Index (at 0.75 mm) ᵖ 960 °C IEC 60695-2-12 - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.