LNP™ ELCRIN™ DMX1234RCC

LNP™ ELCRIN™ DMX1234RCC is an improved scratch-resistant polycarbonate copolymer containing 25% post-consumer recycled content. This standard flow, UV-stabilized, custom-colorable resin is unreinforced and features excellent scratch resistance, impact resistance, and weatherability with no PFAS intentionally added. Suitable for injection molding, it is ideal for a variety of applications, including automotive interiors, sport/leisure, personal accessories, home and commercial appliances, electrical devices and displays, and electrical components and infrastructure.

Brand: LNP™ ELCRIN (71 products)

Polymer Name: Polycarbonate (PC) Copolymer

Processing Methods: Injection Molding

Flexural Modulus: 2503.0 - 2503.0 MPa

Technical Data Sheet

Enhanced TDS

Knowde-enriched technical product data sheet

Identification & Functionality

Chemical Family
Polymer Name
Plastics & Elastomers Functions
Technologies
Product Families

Features & Benefits

Applications & Uses

Properties

Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Stress (Yield, 50 mm/min) ¹77.0MPaISO 527
Tensile Stress (Break, 50 mm/min) ¹61.0MPaISO 527
Tensile Strain (Yield, 50 mm/min) ¹7.0%ISO 527
Tensile Strain (Break, 50 mm/min) ¹92.0%ISO 527
Tensile Modulus (at 1 mm/min) ¹2474.0MPaISO 527
Flexural Modulus (at 2 mm/min) ¹2503.0MPaISO 178
Flexural Stress (Yield, 2 mm/min) ¹108.0MPaISO 178
Tensile Modulus (at 50 mm/min) ¹2630.0MPaASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹80.0%ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹8.0%ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹63.0MPaASTM D638
Tensile Stress (Yield, Type I, 50 mm/min) ¹78.0MPaASTM D638
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹2490.0MPaASTM D790
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹121.0MPaASTM D790
Pencil Hardness Test (0.5 kgf) ¹F-ASTM D3363
Hardness (Rockwell M) ¹89.0-ASTM D785
Physical Properties
ValueUnitsTest Method / Conditions
Density ¹1.18g/cm³ISO 1183
Moisture Absorption (23°C/50% RH/24 hrs) ¹0.04%ASTM D570
Water Absorption (23°C/24hrs) ¹0.09%ASTM D570
Specific Gravity ¹1.18-ASTM D792
Mold Shrinkage (flow, 24 hrs) ¹0.5 - 0.8%ASTM D955
Mold Shrinkage (xflow, 24 hrs) ¹0.5 - 0.8%ASTM D955
Melt Volume Rate (at 300°C/1.2 kg) ¹14.0cm³/10 minISO 1133
Melt Volume Rate (at 300°C/1.2 kg) ¹14.0cm³/10 minASTM D1238
Melt Flow Rate (at 300°C/1.2 kgf) ¹16.0g/10 minASTM D1238
Thermal Properties
ValueUnitsTest Method / Conditions
Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹118.0°CISO 75/Af
Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹132.0°CISO 75/Bf
Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹120.0°CASTM D648
Heat Deflection Temperature (0.45 MPa, 3.2 mm, unannealed) ¹133.0°CASTM D648
Vicat Softening Temperature (at Rate B/50) ¹138.0°CISO 306
Vicat Softening Temperature (at Rate B/50) ¹138.0°CASTM D1525
Vicat Softening Temperature (at Rate B/120) ¹140.0°CISO 306
Vicat Softening Temperature (at Rate B/120) ¹140.0°CASTM D1525
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹6.8e-051/°CISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹6.8e-051/°CASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹7.0e-051/°CISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹7.0e-051/°CASTM E831
Impact Properties
ValueUnitsTest Method / Conditions
Izod Impact (Notched 80*10*3 +23°C) ¹3.0kJ/m²ISO 180/1A
Izod Impact (Notched 80*10*3 -30°C) ¹20.0kJ/m²ISO 180/1A
Izod Impact (Unnotched 80*10*3 +23°C) ¹169.0kJ/m²ISO 180/1U
Izod Impact (Unnotched 80*10*3 -30°C )¹87.0kJ/m²ISO 180/1U
Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹2.0kJ/m²ISO 179/1eA
Charpy Impact (at -30°C, V-notch Edgew 80*10*3 sp=62mm) ¹1.0kJ/m²ISO 179/1eA
Charpy Impact (at 23°C, Unnotch Edgew 80*10*3 sp=62mm) ¹324.0kJ/m²ISO 179/1eU
Charpy Impact (at -30°C, Unnotch Edgew 80*10*3 sp=62mm) ¹93.0kJ/m²ISO 179/1eU
Izod Impact (Notched, 23°C) ¹30.0J/mASTM D256
Izod Impact (Notched, 0°C) ¹32.0J/mASTM D256
Izod Impact (Notched, -30°C) ¹31.0J/mASTM D256
Izod Impact (Unnotched, 23°C) ¹NBJ/mASTM D4812
Izod Impact (Unnotched, -30°C) ¹1440.0J/mASTM D4812
Instrumented Dart Impact Total Energy (at 23°C) ¹39.0JASTM D3763
Injection Molding
ValueUnitsTest Method / Conditions
Drying Temperature ²120.0°C-
Drying Time ²3 - 4Hrs-
Maximum Moisture Content ²0.02%-
Melt Temperature ²295 - 315°C-
Rear - Zone 1 Temperature ²260 - 280°C-
Middle - Zone 2 Temperature ²280 - 305°C-
Front - Zone 3 Temperature ²295 - 315°C-
Nozzle Temperature ²290 - 310°C-
Mold Temperature ²70 - 95°C-
Note

¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
² ;Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.