Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ 51 MPa ASTM D638 Tensile Strain (Break, Type I, 50 mm/min) ¹¹ 300 % ASTM D638 Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ 82 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ 2340 MPa ASTM D790 Hardness (Rockwell R) ¹¹ 117 - ASTM D785 - Physical Properties
Value Units Test Method / Conditions Specific Gravity ¹¹ 1.31 - ASTM D792 Specific Volume ¹¹ 0.76 cm³/g ASTM D792 Water Absorption (at 23°C, 24hrs) ¹¹ 0.08 % ASTM D570 Mold Shrinkage (flow, 0.75-2.3 mm) ᵍ ¹¹ 0.9 - 1.6 % SABIC method Mold Shrinkage (flow, 2.3-4.6 mm) ᵍ ¹¹ 1.5 - 2.3 % SABIC method Mold Shrinkage (xflow, 0.75-2.3 mm) ᵍ ¹¹ 1 - 1.7 % SABIC method Mold Shrinkage (xflow, 2.3-4.6 mm) ᵍ ¹¹ 1.6 - 2.4 % SABIC method Melt Volume Rate (at 250°C, 2.16 kg) ¹¹ 9 cm³/10 min ASTM D1238 Melt Volume Rate (at 250°C, 2.16 kg) ¹¹ 9 cm³/10 min ISO 1133 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ 154 °C ASTM D648 Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ 54 °C ASTM D648 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ 0.000081 1/°C ASTM E831 Coefficient of Thermal Expansion (at 60°C to 138°C, flow) ¹¹ 0.00014 1/°C ASTM E831 - Electrical Properties
Value Units Test Method / Conditions Volume Resistivity ¹¹ min. 4.E+16 Ω.cm ASTM D257 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, at 23°C) ¹¹ 1602 J/m ASTM D4812 Izod Impact (Notched, at 23°C) ¹¹ 53 J/m ASTM D256 Modified Gardner (at 23°C) ¹¹ 40 J ASTM D3029 - Processing Information (Compounding Extrusion)
Value Units Test Method / Conditions Adapter Temperature 240 - 275 °C - Barrel - Zone 1 Temperature 200 - 230 °C - Barrel - Zone 2 Temperature 240 - 255 °C - Barrel - Zone 3 Temperature 240 - 275 °C - Barrel - Zone 4 Temperature 240 - 275 °C - Die Temperature 240 - 275 °C - Drying Temperature 110 - 120 °C - Drying Time 4 - 6 Hrs - Drying Time (Cumulative) 8 Hrs - Maximum Moisture Content 0.02 % - Melt Temperature 245 - 260 °C - Water Bath Temperature 25 - 35 °C - - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.