Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ 62 MPa ASTM D638 Tensile Stress (Break, Type I, 50 mm/min) ¹¹ 68 MPa ASTM D638 Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ 7 % ASTM D638 Tensile Strain (Break, Type I, 50 mm/min) ¹¹ 130 % ASTM D638 Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ 96 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ 2340 MPa ASTM D790 Hardness (Rockwell M) ¹¹ 70 - ASTM D785 Hardness (Rockwell R) ¹¹ 118 - ASTM D785 Taber Abrasion (CS-17, 1 kg) ¹¹ 1.00E+01 mg/1000cy ASTM D1044 - Physical Properties
Value Units Test Method / Conditions Specific Gravity ¹¹ 1.2 - ASTM D792 Specific Volume ¹¹ 0.83 cm³/g ASTM D792 Density ¹¹ 1.19 g/cm³ ASTM D792 Water Absorption (at 23°C, 24hrs) ¹¹ 0.15 % ASTM D570 Water Absorption (at 23°C, saturated) ¹¹ 0.35 % ASTM D570 Water Absorption (Equilibrium, at 100°C) ¹¹ 0.58 % ASTM D570 Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ 0.5 - 0.7 % SABIC method Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ 10.5 g/10 min ASTM D1238 - Thermal Properties
Value Units Test Method / Conditions Vicat Softening Temperature (Rate B/50) ¹¹ 154 °C ASTM D1525 Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ 137 °C ASTM D648 Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ 132 °C ASTM D648 Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹ 0.0000684 1/°C ASTM E831 Specific Heat ¹¹ 1.25 J/g-°C ASTM C351 Thermal Conductivity ¹¹ 0.27 W/m-°C ASTM C177 Relative Temperature Index (Electrical) ᵖ ¹¹ 130 °C UL 746B Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ 130 °C UL 746B Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ 130 °C UL 746B - Electrical Properties
Value Units Test Method / Conditions Volume Resistivity ¹¹ 1.00E+17 Ω.cm ASTM D257 Dielectric Strength (in air, at 3.2mm) ¹¹ 14.9 kV/mm ASTM D149 Relative Permittivity (50/60 Hz) ¹¹ 3.17 - ASTM D150 Relative Permittivity (1 MHz) ¹¹ 2.96 - ASTM D150 Dissipation Factor (at 50/60 Hz) ¹¹ 0.0009 - ASTM D150 Dissipation Factor (at at 1 MHz) ¹¹ 0.01 - ASTM D150 High Voltage Arc Track Rate (PLC) ¹¹ 4 PLC Code UL 746A Comparative Tracking Index (UL, PLC) ¹¹ 2 PLC Code UL 746A Hot Wire Ignition (PLC 2) ¹¹ min. 1.5 mm UL 746A Hot Wire Ignition (PLC 3) ¹¹ min. 1.1 mm UL 746A High Ampere Arc Ignition (PLC 0) ¹¹ min. 1.5 mm UL 746A High Ampere Arc Ignition (PLC 1) ¹¹ min. 3 mm UL 746A High Ampere Arc Ignition (PLC 2) ¹¹ min. 1.1 mm UL 746A - Optical Properties
Value Units Test Method / Conditions Light Transmission (at 2.54 mm) ¹¹ 88 % ASTM D1003 Haze (at 2.54 mm) ¹¹ 1 % ASTM D1003 Refractive Index ¹¹ 1.586 - ASTM D542 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Unnotched, at 23°C) ¹¹ 3204 J/m ASTM D4812 Izod Impact (Notched, at 23°C) ¹¹ 801 J/m ASTM D256 Tensile Impact Strength (Type S) ¹¹ 577 kJ/m² ASTM D1822 Falling Dart Impact (at 23°C) ¹¹ 169 J ASTM D3029 Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ 63 J ASTM D3763 - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 120 °C - Drying Time ⁷ 3 - 4 Hrs - Drying Time (Cumulative) ⁷ 48 Hrs - Maximum Moisture Content ⁷ 0.02 % - Melt Temperature ⁷ 295 - 315 °C - Nozzle Temperature ⁷ 290 - 310 °C - Front - Zone 3 Temperature ⁷ 295 - 315 °C - Middle - Zone 2 Temperature ⁷ 280 - 305 °C - Rear - Zone 1 Temperature ⁷ 270 - 295 °C - Mold Temperature ⁷ 70 - 95 °C - Back Pressure ⁷ 0.3 - 0.7 MPa - Screw Speed ⁷ 40 - 70 rpm - Shot to Cylinder Size ⁷ 40 - 60 % - Vent Depth ⁷ 0.025 - 0.076 mm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized (94HB Flame Class Rating) ᵖ min. 0.7 mm UL 94 Oxygen Index (LOI) ᵖ 25 % ISO 4589 UV-light (Water exposure/immersion) ᵖ F2 - UL 746C - Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Regional Availability