Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ 51 MPa ASTM D638 Tensile Stress (Break, Type I, 50 mm/min) ¹¹ 46 MPa ASTM D638 Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ 5 % ASTM D638 Tensile Strain (Break, Type I, 50 mm/min) ¹¹ 66 % ASTM D638 Tensile Modulus (at 50 mm/min) ¹¹ 2040 MPa ASTM D638 Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ 80 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ 1990 MPa ASTM D790 - Physical Properties
Value Units Test Method / Conditions Density ¹¹ 1.3 g/cm³ ISO 1183 Melt Volume Rate (at 300°C, 1.2 kg) ¹¹ 15 cm³/10 min ISO 1133 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ 114 °C ASTM D648 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched, at 23°C) ¹¹ 530 J/m ASTM D256 - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁷ 120 °C - Drying Time ⁷ 3 - 4 Hrs - Maximum Moisture Content ⁷ 0.02 % - Melt Temperature ⁷ 295 - 315 °C - Nozzle Temperature ⁷ 290 - 310 °C - Front - Zone 3 Temperature ⁷ 295 - 315 °C - Middle - Zone 2 Temperature ⁷ 280 - 305 °C - Rear - Zone 1 Temperature ⁷ 260 - 280 °C - Hopper Temperature ⁷ 60 - 80 °C - Mold Temperature ⁷ 70 - 95 °C - - Note
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.