Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Break, Type I, 50 mm/min) ¹¹ 23 MPa ASTM D638 Tensile Strain (Break, Type I, 50 mm/min) ¹¹ 85 % ASTM D638 Flexural Modulus (at 12.5 mm/min, 100 mm span) ¹¹ 650 MPa ASTM D790 Tensile Stress (Break, 50 mm/min) ¹¹ 23 MPa ISO 527 Tensile Strain (Break, 50 mm/min) ¹¹ 90 % ISO 527 Flexural Modulus (at 12.5 mm/min) ¹¹ 720 MPa ISO 178 Hardness (Shore D) ¹¹ 56 - ISO 868 Tear Strength ¹¹ 25 N/mm ISO 6383 - Physical Properties
Value Units Test Method / Conditions Specific Gravity ¹¹ 1.03 - ASTM D792 Water Absorption (at 23°C, 48hrs) ¹¹ 0.1 % ASTM D570 Melt Flow Rate (at 250°C, 10.0 kgf) ¹¹ 5.1 g/10 min ASTM D1238 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ 85 °C ASTM D648 Vicat Softening Temperature (Rate A/50) ¹¹ 102 °C ISO 306 - Typical Properties
Value Units Test Method / Conditions Tensile Strength (Break) ¹⁹ 33 MPa UL 1581 Tensile Elongation (Break) ¹⁹ 197 % UL 1581 Tensile Strength (Break, after 7days, at 136°C) ¹⁹ 36 MPa UL 1581 Tensile Elongation (Break, after 7days, at 136°C) ¹⁹ 156 % UL 1581 UL Temperature Rating ¹⁹ 105 °C UL 1581 Heat Deformation (at 121°C, 250g) ¹⁹ 26 % UL 1581 VW-1 ¹⁹ Pass - UL 1581 - Electrical Properties
Value Units Test Method / Conditions Volume Resistivity ¹¹ 3.90E+16 Ω.cm IEC 60093 Dielectric Strength (in oil, at 2mm) ¹¹ 26 kV/mm IEC 60243-1 Relative Permittivity (1 MHz) ¹¹ 2.5 - IEC 60250 Dissipation Factor (at 50/60 Hz) ¹¹ 0.024 - IEC 60250 Dissipation Factor (at at 1 MHz) ¹¹ 0.0038 - IEC 60250 Comparative Tracking Index ¹¹ 600 V IEC 60112 Relative Permittivity (50/60 Hz) ¹¹ 2.6 - IEC 60250 - Impact Properties
Value Units Test Method / Conditions Brittleness Temperature ¹¹ max. -40 °C ASTM D746 - Flame Characteristics
Value Units Test Method / Conditions Oxygen Index (LOI) 25 % ISO 4589 Smoke Density (on 0.5mm plaque, Non-Flame, Ds-max) 75 - ASTM E662 Smoke Density (on 0.5mm plaque, Flame, Ds-max) 150 - ASTM E662 Glow Wire Flammability Index (passes at 960°C) 3 mm IEC 60695-2-12 Glow Wire Ignitability Temperature (at 3.0 mm) 750 °C IEC 60695-2-13 - Wire Coating Extrusion
Value Units Test Method / Conditions Conductor Pre-heat Temperature 80 - 150 °C - Cooling Water Air Gap 100 - 200 mm - Cross-head Temperature 250 - 285 °C - Die Temperature 250 - 285 °C - Drying Temperature 60 - 80 °C - Drying Time 4 - 6 Hrs - Drying Time (Cumulative) 12 Hrs - Extruder Length/Diameter Ratio (L/D) 22:1 to 26:1 - - Feed Zone Temperature 210 - 260 °C - Head Zone Temperature 250 - 285 °C - Maximum Moisture Content 0.02 % - Melt Temperature 250 - 285 °C - Middle Zone Temperatures 230 - 285 °C - Neck Temperature 250 - 285 °C - Screen Pack 150 - 100 - - Screw Speed 15 - 40 rpm - Water Bath Temperature 15 - 80 °C - - Note
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ¹⁹ Wire and cable - UL 1581 tested on 2.0mm wire with 0.12mmx20 stranded copper
Regulatory & Compliance
- Certifications & Compliance