Properties
- Physical Form
- Physical Properties
Value Units Test Method / Conditions Density (23 °C, 50 % RH) 1.15 g/cm³ DIN EN ISO 1133 - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break (50 mm/min 23 °C) min. 50 % DIN EN ISO 527 Flexural Modulus (2 mm/min 23 °C) 1950 MPa DIN EN ISO 178 Flexural Strength (2 mm/min 23 °C) 75 MPa DIN EN ISO 178 Impact Strength (Charpy) n.b. kJ/m² DIN EN ISO 179/1eU Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) 50 kJ/m² DIN EN ISO 179/1eA Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) 40 kJ/m² DIN EN ISO 179/1eA Tensile Modulus (1 mm/min 23 °C) 2100 MPa DIN EN ISO 527 Tensile Strength (50 mm/min 23 °C) 49 MPa DIN EN ISO 527 - Thermal Properties
Value Units Test Method / Conditions Vicat Softening Temperature (B 50) 114 °C DIN EN ISO 306 Flammability (own test) HB - UL94 Heat deflection temperature (HDT/A) 80 °C DIN EN ISO 75-1 Melt Mass-Flow Rate (MFR) 23 g/10 min DIN EN ISO 1133 Processing Shrinkage (220 °C, 10 kg) 0.5 0.7 % DIN EN ISO 294-4