| Density | 2.05 | g/cm3 | ISO 1183 |
| Flexural Strength (Perpendicular) | 600 | MPa | ISO 178 |
| Flexural Strength at 150°C (Perpendicular) | 500 | MPa | ISO 178 |
| Modulus of Elasticity In Flexion (Perpendicular) | 30000 | MPa | ISO 178 |
| Modulus of Elasticity In Flexion at 150°C (Perpendicular) | 26000 | MPa | ISO 178 |
| Compressive Strength (Perpendicular) | 600 | MPa | ISO 604 |
| Compressive Strength (Perpendicular) | 450 | MPa | ISO 604 |
| Tensile Strength (Perpendicular) | 450 | MPa | ISO 527 |
| Impact Strength (Perpendicular) | 300 | kJ/m2 (Charpy) | ISO 179 |
| Water Absorption (Method 1) | max. 0,2 | % | ISO 62 |
| Flammability (3mm) | V0 | / | UL 94 |
| Temperature Index | 180 | T.I. | IEC 60216 |
| Insulation Class | H | / | IEC 60085 |
| Electric Strength as 90°C under Oil (Perpendicular) | 13 | kV/mm | IEC 60243 |
| Electric Strength as 90°C under Oil (Perpendicular) | 70 | kV/25mm | IEC 60243 |
| Relative Permittivity (50 Hz) | 5 | εr | IEC 60250 |
| Dielectric Loss Factor (50 Hz) | 0.04 | tan δ | IEC 60250 |
| Specific Surface Resistance | 1012 | Ω | IEC 60093 |
| Specific Volume Resistance | 10^14 | Ohm-cm | IEC 60093 |
| Comparative Tracking Index (Test Solution A) | 600 | CTI | IEC 60112 |
| Insulation Resistance After 24 H Water Immersion | 1010 | Ω | IEC 60167 |