Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
- Processing Method
Injection Molding
- Filler and Reinforcement
- Filler : Glass Fiber
- Reinforcement : 30% Filler by Weight
Features & Benefits
- Materials Features
- Features
- Good Dimensional Stability
- Good Stiffness
- High Heat Resistance
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
- Physical Properties
Value Units Test Method / Conditions Density 1.52 - ASTM D792 Melt Mass Flow Rate (at 250°C, 2.16 kg) 8.0 - 20 g/10 min ASTM D1238 Molding Shrinkage (at 0.125 in, Flow) 6.0E-3 to 9.0E-3 in/in ASTM D955 Specific Gravity 1.52 - ASTM D792 - Mechanical Properties
Value Units Test Method / Conditions Tensile Strength (at Yield, 0.125 in) 17000 psi ASTM D638 Tensile Strength (at Break, 0.125 in) 17000 psi ASTM D638 Flexural Modulus (at 0.125 in) 1100000 psi ASTM D790 Flexural Strength (at Break, 0.125 in) 28000 psi ASTM D790 - Thermal Properties
Value Units Test Method / Conditions Deflection Temperature Under Load (at 66 psi, 0.125 in, Unannealed) 425 °F ASTM D648 Deflection Temperature Under Load (at 264 psi, 0.125 in, Unannealed) 395 °F ASTM D648 Relative Thermal Index Electrical Property (at 0.06 in) 167 °F UL 746 Relative Thermal Index Electrical Property (at 0.12 in) 167 °F UL 746 Relative Thermal Index Impact Property (at 0.06 in) 167 °F UL 746 Relative Thermal Index Impact Property (at 0.12 in) 167 °F UL 746 Relative Thermal Index Strength Property (at 0.06 in) 167 °F UL 746 Relative Thermal Index Strength Property (at 0.12 in) 167 °F UL 746 - Electrical Properties
Value Units Test Method / Conditions Comparative Tracking Index (at 0.0591 in) PLC 1 - UL 746 High Amp Arc Ignition (at 0.06 in) PLC 2 - UL 746 High Amp Arc Ignition (at 0.12 in) PLC 2 - UL 746 Hot Wire Ignition (at 0.06 in) PLC 2 - UL 746 Hot Wire Ignition (at 0.12 in) PLC 1 - UL 746 - Flammability
Value Units Test Method / Conditions Flame Rating (at 0.06 in) HB - UL 94 Flame Rating (at 0.12 in) HB - UL 94 - Processing Information (Injection Molding)
Value Units Test Method / Conditions Drying Temperature 240 - 250 °F - Drying Time 3.0 - 4.0 hr - Front Temperature 480 - 510 °F - Middle Temperature 470 - 500 °F - Mold Temperature 150 - 190 °F - Rear Temperature 460 - 490 °F - Maximum Drying Time 8 hr - Processing Temperature (Melt) 450 - 500 °F - - Impact Properties
Value Units Test Method / Conditions Impact Strength (at 73°F, 0.125 in, Notched Izod) 1 ft·lb/in ASTM D256
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
- Agency Ratings & Compliance
RoHS Compliant