Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Plastics & Elastomers Functions
- Technologies
- Product Families
- Processing Method
Injection Molding
- Additive
Flame Retardant
- Filler and Reinforcement
Mineral
Features & Benefits
- Labeling Claims
- Materials Features
- Features
- Bromine Free
- Chlorine Free
- Flame Retardant
- Medium Heat Resistance
- Self Extinguishing
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
- Physical Properties
Value Units Test Method / Conditions Density 1.24 - ASTM D792 Melt Mass Flow Rate (at 250°C, 11.6 kg) 15 - 25 g/10 min ASTM D1238 Molding Shrinkage (Flow) 5.0E-3 to 7.0E-3 in/in ASTM D955 Specific Gravity 1.24 - ASTM D792 - Mechanical Properties
Value Units Test Method / Conditions Tensile Strength (at Yield, 0.125 in) 9000 psi ASTM D638 Tensile Strength (at Break, 0.125 in) 8000 psi ASTM D638 Tensile Elongation (at Yield, 0.125 in) 7 % ASTM D638 Tensile Elongation (at Break, 0.125 in) 30 % ASTM D638 Flexural Modulus (at 0.125 in) 415000 psi ASTM D790 Flexural Strength (at 0.125 in) 14000 psi ASTM D790 - Thermal Properties
Value Units Test Method / Conditions Deflection Temperature Under Load (at 66 psi, 0.125 in, Unannealed) 190 °F ASTM D648 Deflection Temperature Under Load (at 264 psi, 0.125 in, Unannealed) 180 °F ASTM D648 Vicat Softening Temperature 240 °F ASTM D1525 ² - Electrical Properties
Value Units Test Method / Conditions Volume Resistivity 10000000000000000 ohms·cm ASTM D257 - Processing Information (Injection Molding)
Value Units Test Method / Conditions Drying Temperature 220 - 230 °F - Drying Time 3.0 - 4.0 hr - Front Temperature 470 - 540 °F - Middle Temperature 450 - 530 °F - Mold Temperature 150 - 180 °F - Rear Temperature 430 - 520 °F - Maximum Drying Time 8 hr - Processing Temperature (Melt) 475 - 540 °F - - Impact Properties
Value Units Test Method / Conditions Impact Strength (at 73°F, 0.125 in, Notched Izod) 2 ft·lb/in ASTM D256 - Hardness
Value Units Test Method / Conditions Rockwell Hardness (R-Scale) 121 - ASTM D785
Regulatory & Compliance
- Certifications & Compliance
- Agency Ratings & Compliance
RoHS Compliant