Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Plastics & Elastomers Functions
- Technologies
- Product Families
- Processing Method
Structural Foam Molding
- Additive
Flame Retardant
- Filler and Reinforcement
- Filler : Glass Fiber
- Reinforcement : 10% Filler by Weight
Features & Benefits
- Materials Features
- Features
- Flame Retardant
- Foamable
- Good Impact Resistance
- High Heat Resistance
- Medium Heat Resistance
- Self Extinguishing
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Uses
Structural Foam
Properties
- Physical Form
- Physical Properties
Value Units Test Method / Conditions Density 1.27 - ASTM D792 Melt Mass Flow Rate (at 300°C, 1.2 kg) 5.0 - 12 g/10 min ASTM D1238 Molding Shrinkage (at 0.125 in, Flow) 3.0E-3 to 6.0E-3 in/in ASTM D955 Specific Gravity 1.27 - ASTM D792 - Mechanical Properties
Value Units Test Method / Conditions Tensile Strength (at Yield, 0.125 in) 9500 psi ASTM D638 Tensile Strength (at Break, 0.125 in) 9150 psi ASTM D638 Flexural Modulus (at 0.125 in) 550000 psi ASTM D790 Flexural Strength (at 0.125 in) 15800 psi ASTM D790 - Thermal Properties
Value Units Test Method / Conditions Deflection Temperature Under Load (at 66 psi, 0.125 in, Unannealed) 290 °F ASTM D648 Deflection Temperature Under Load (at 264 psi, 0.125 in, Unannealed) 280 °F ASTM D648 Relative Thermal Index Electrical Property (at 0.24 in) 176 °F UL 746 Relative Thermal Index Impact Property (at 0.24 in) 176 °F UL 746 Relative Thermal Index Strength Property (at 0.24 in) 176 °F UL 746 - Flammability
Value Units Test Method / Conditions Flame Rating (at 0.24 in, All) V-0 - UL 94 - Processing Information (Injection Molding)
Value Units Test Method / Conditions Drying Temperature 245 - 255 °F - Drying Time 3.0 - 4.0 hr - Front Temperature 560 - 590 °F - Middle Temperature 560 - 590 °F - Mold Temperature 160 - 220 °F - Maximum Drying Time 8 hr - Rear Temperature 490 - 510 °F - Processing Temperature (Melt) 550 - 600 °F - - Impact Properties
Value Units Test Method / Conditions Impact Strength (at 73°F, 0.125 in, Notched Izod) 2 ft·lb/in ASTM D256
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
- Agency Ratings & Compliance
RoHS Compliant