Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Plastics & Elastomers Functions
- Technologies
- Product Families
- Processing Method
Injection Molding
- Additive
Mold Release
- Filler and Reinforcement
- Filler : Glass Fiber
- Reinforcement : 10% Filler by Weight
Features & Benefits
- Materials Features
- Features
- Flame Retardant
- Good Mold Release
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
- Physical Properties
Value Units Test Method / Conditions Density 1.26 - ASTM D792 Melt Mass Flow Rate (at 300°C, 1.2 kg) 5.0 - 12 g/10 min ASTM D1238 Molding Shrinkage (at 0.125 in, Flow) 2.0E-3 to 5.0E-3 in/in ASTM D955 Molding Shrinkage (at 0.125 in, Across Flow) 2.0E-3 to 5.0E-3 in/in ASTM D955 Specific Gravity 1.26 - ASTM D792 - Mechanical Properties
Value Units Test Method / Conditions Tensile Strength (at Yield, 0.125 in) 9500 psi ASTM D638 Tensile Strength (at Break, 0.125 in) 8100 psi ASTM D638 Tensile Elongation (at Yield, 0.125 in) 6 % ASTM D638 Tensile Elongation (at Break, 0.125 in) 15 % ASTM D638 Flexural Modulus (at 0.125 in) 490000 psi ASTM D790 Flexural Strength (at 0.125 in) 14900 psi ASTM D790 - Thermal Properties
Value Units Test Method / Conditions Deflection Temperature Under Load (at 66 psi, 0.125 in, Unannealed) 290 °F ASTM D648 Deflection Temperature Under Load (at 264 psi, 0.125 in, Unannealed) 280 °F ASTM D648 Relative Thermal Index Electrical Property (at 0.06 in) 176 °F UL 746 Relative Thermal Index Electrical Property (at 0.12 in) 176 °F UL 746 Relative Thermal Index Impact Property (at 0.06 in) 176 °F UL 746 Relative Thermal Index Impact Property (at 0.12 in) 176 °F UL 746 Relative Thermal Index Strength Property (at 0.06 in) 176 °F UL 746 Relative Thermal Index Strength Property (at 0.12 in) 176 °F UL 746 Vicat Softening Temperature 305 °F ASTM D1525 ² - Electrical Properties
Value Units Test Method / Conditions Comparative Tracking Index (at 0.0591 in) PLC 3 - UL 746 High Amp Arc Ignition (at 0.06 in) PLC 1 - UL 746 High Amp Arc Ignition (at 0.12 in) PLC 1 - UL 746 Hot Wire Ignition (at 0.06 in) PLC 2 - UL 746 Hot Wire Ignition (at 0.12 in) PLC 1 - UL 746 - Flammability
Value Units Test Method / Conditions Flame Rating (at 0.06 in, All) V-0 - UL 94 Flame Rating (at 0.12 in, All) V-0, 5VA - UL 94 - Processing Information (Injection Molding)
Value Units Test Method / Conditions Drying Temperature 245 - 255 °F - Drying Time 3.0 - 4.0 hr - Front Temperature 600 - 640 °F - Middle Temperature 580 - 620 °F - Mold Temperature 180 - 240 °F - Rear Temperature 560 - 600 °F - Maximum Drying Time 8 hr - Processing Temperature (Melt) 575 - 625 °F - - Impact Properties
Value Units Test Method / Conditions Impact Strength (at 73°F, 0.125 in, Notched Izod) 2 ft·lb/in ASTM D256 - Hardness
Value Units Test Method / Conditions Rockwell Hardness (M-Scale) 85 - ASTM D785 Rockwell Hardness (R-Scale) 124 - ASTM D785
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
- Agency Ratings & Compliance
RoHS Compliant