Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Plastics & Elastomers Functions
- Technologies
- Product Families
- Processing Method
Injection Molding
Features & Benefits
- Labeling Claims
- Materials Features
- Features
- Food Contact Acceptable
- General Purpose
- High Flow
- High Impact Resistance
- Medium Heat Resistance
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
- Physical Properties
Value Units Test Method / Conditions Density 1.2 - ASTM D792 Melt Mass Flow Rate (at 300°C, 1.2 kg) 14 - 20 g/10 min ASTM D1238 Molding Shrinkage (at 0.125 in, Flow) 5.0E-3 to 7.0E-3 in/in ASTM D955 Molding Shrinkage (at 0.125 in, Across Flow) 5.0E-3 to 7.0E-3 in/in ASTM D955 Specific Gravity 1.2 - ASTM D792 - Mechanical Properties
Value Units Test Method / Conditions Tensile Strength (at Yield, 0.125 in) 9000 psi ASTM D638 Tensile Strength (at Break, 0.125 in) 10000 psi ASTM D638 Tensile Elongation (at Yield, 0.125 in) 6 % ASTM D638 Tensile Elongation (at Break, 0.125 in) 120 % ASTM D638 Flexural Modulus (at 0.125 in) 335000 psi ASTM D790 Flexural Strength (at 0.125 in) 13900 psi ASTM D790 - Thermal Properties
Value Units Test Method / Conditions Deflection Temperature Under Load (at 66 psi, 0.125 in, Unannealed) 270 °F ASTM D648 Deflection Temperature Under Load (at 264 psi, 0.125 in, Unannealed) 260 °F ASTM D648 Vicat Softening Temperature 300 °F ASTM D1525 ² - Optical Properties
Value Units Test Method / Conditions Light Transmittance (at 100 mil) 88 % ASTM D1003 Haze (at 100 mil) 1 % ASTM D1003 - Processing Information (Injection Molding)
Value Units Test Method / Conditions Drying Temperature 245 - 255 °F - Drying Time 3.0 - 4.0 hr - Front Temperature 540 - 580 °F - Middle Temperature 520 - 560 °F - Mold Temperature 160 - 200 °F - Rear Temperature 500 - 540 °F - Maximum Drying Time 8 hr - Processing Temperature (Melt) 550 - 600 °F - - Impact Properties
Value Units Test Method / Conditions Impact Strength (at 73°F, 0.125 in, Notched Izod) 13 ft·lb/in ASTM D256 Gardner Impact Strength (at 0.125 in) min. 320 in·lb ASTM D3029 - Hardness
Value Units Test Method / Conditions Rockwell Hardness (M-Scale) 70 - ASTM D785 Rockwell Hardness (R-Scale) 118 - ASTM D785