Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
- Processing Method
Injection Molding
- Filler and Reinforcement
- Filler : Glass Fiber
- Reinforcement : 10% Filler by Weight
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
- Physical Properties
Value Units Test Method / Conditions Density 1.1 - ASTM D792 Melt Mass Flow Rate (at 230°C, 3.8 kg) 0.10 - 5.0 g/10 min ASTM D1238 Molding Shrinkage (at 0.125 in, Flow) 1.0E-3 to 4.0E-3 in/in ASTM D955 Specific Gravity 1.1 - ASTM D792 - Mechanical Properties
Value Units Test Method / Conditions Tensile Strength (at Yield, 0.125 in) 6900 psi ASTM D638 Tensile Strength (at Break, 0.125 in) 6700 psi ASTM D638 Flexural Modulus (at 0.125 in) 445000 psi ASTM D790 Flexural Strength (at Break, 0.125 in) 11000 psi ASTM D790 - Thermal Properties
Value Units Test Method / Conditions Deflection Temperature Under Load (at 66 psi, 0.125 in, Unannealed) 210 °F ASTM D648 Deflection Temperature Under Load (at 264 psi, 0.125 in, Unannealed) 195 °F ASTM D648 - Processing Information (Injection Molding)
Value Units Test Method / Conditions Drying Temperature 175 - 185 °F - Drying Time 3.0 - 4.0 hr - Front Temperature 410 - 440 °F - Middle Temperature 410 - 430 °F - Mold Temperature 120 - 140 °F - Maximum Drying Time 8 hr - Rear Temperature 375 - 390 °F - Processing Temperature (Melt) 440 - 460 °F - - Impact Properties
Value Units Test Method / Conditions Impact Strength (at 0.125 in, Notched Izod) 1 ft·lb/in ASTM D256
Regulatory & Compliance
- Certifications & Compliance
- Agency Ratings & Compliance
RoHS Compliant