Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Application Area
- Applications
- For locking and sealing of threaded metal pipes and fittings
- Ideal for pneumatic and hydraulic connections
- Directions for Use
Surfaces should be dry, clean and free of any contamination. Apply 360° bead of product to the leading threads of the male fitting, leaving the first thread free. Force the material into the threads and voids, adjust product amount accordingly and apply a 360° bead of product on the female threads also. Assemble and tighten as required.
Properties
- Color
- Physical Properties
Value Units Test Method / Conditions Coefficient of Thermal Expansion 80x10⁻⁶ K-1 ASTM D 696 Coefficient of Thermal Conductivity 0.1 W/(m.K) ASTM C 177 Specific Heat 0.3 kJ/(kg.K) - - Typical Properties
Value Units Test Method / Conditions Loctite® Equivalent 545.0 - - Permatex® Equivalent 54550.0 - - - Chemical Resistance
Value Units Test Method / Conditions Initial Strength Retained for Acetone (at 22ºC, 500hrs) 95 % - Initial Strength Retained for Ethanol (at 22ºC, 500hrs) 100 % - Initial Strength Retained for Motor Oil (at 125ºC, 500hrs) 100 % - Initial Strength Retained for Gasoline (at 22ºC, 500hrs) 100 % - Initial Strength Retained for Brake Fluid (at 22ºC, 500hrs) 100 % - Initial Strength Retained for Water/Glycol (at 87ºC, 500hrs) 100 % - Initial Strength Retained for Acetone (at 22ºC, 1000hrs) 95 % - Initial Strength Retained for Ethanol (at 22ºC, 1000hrs) 90 % - Initial Strength Retained for Motor Oil (at 125ºC, 1000hrs) 100 % - Initial Strength Retained for Gasoline (at 22ºC, 1000hrs) 95 % - Initial Strength Retained for Brake Fluid (at 22ºC, 1000hrs) 95 % - Initial Strength Retained for Water/Glycol (at 87ºC, 1000hrs) 100 % - - Cured Properties
Value Units Test Method / Conditions Handling Cure Time 10 - 30 minutes - Functional Cure Time 2 - 4 hrs - Full Cure Time 24 hrs - Breakaway Torque (M10 Steel Nuts and Bolts) 2 (20) N.m (lbs.in) ISO 10964 Prevail Torque (M10 Steel Nuts and Bolts) 2 (20) N.m (lbs.in) ISO 10964 Break Loose Torque (M10 Steel Nuts and Bolts, Pre-Torqued to 5 Nm) 5 (44) N.m (lbs.in) ISO 10964 Maximum Prevail Torque (M10 Steel Nuts and Bolts, Pre-Torqued to 5 Nm) 5 (44) N.m (lbs.in) ISO 10964 Compressive Shear Strength of Steel Pins and Collars min. 1.5 (220) N/mm² (psi) ISO 10123 Operating Pressure 10000 psi - Temperature Range -65 to 300 ºF - - Adhesive Properties
Value Units Test Method / Conditions Composition Methacrylate ester - - Viscosity (at 20 rpm, 25ºC, Brookfield RVT Spindle 3) 14000 cPs - Specific Gravity 1.2 - - Flash Point min. 100 ºC - Solvent Content None - -
Safety & Health
- Precautions
This product and the auxiliary materials normally combined with it are capable of producing adverse health effects ranging from minor skin irritation to serious systemic effects. None of these materials should be used, stored, or transported until the handling precautions and recommendations as stated in the Material Safety Data Sheets (MSDS).
Storage & Handling
- Storage Information
Anaerobic adhesives are ideally stored in a cool, dry place in unopened containers at room temperature, 46°F to 82°F. Do not return unused material to its original container.