- Ideal for applications where the temperatures range from -65 to 450 º F
- Ideal for thread locking heavy duty applications such as bolts up to 1 ½” (36 mm) used in transmission, construction equipment or railroad assemblies, etc
- Lubricated for easy assembly. Prevents loosening and leakage of threaded fasteners. Locks and seals threaded joints-nuts, screws, and studs. To disassemble, apply high heat and use tools
- Application Method
Surfaces should be dry, clean, and free of any contamination. Thread locker should be applied to the bolt in sufficient quantity to fill threads. This thread locker is specifically formulated to give controlled friction and torque/tension ratio during assembly.
Properties
- Color
- Physical Properties
Value Units Test Method / Conditions Coefficient of Thermal Expansion 80x10⁻⁶ K-1 ASTM D 696 Coefficient of Thermal Conductivity 0.1 W/(m.K) ASTM C 177 Specific Heat 0.3 kJ/(kg.K) - - Typical Properties
Value Units Test Method / Conditions Loctite® Equivalent 272.0 - - - Chemical Resistance
Value Units Test Method / Conditions Initial Strength Retained for Acetone (at 22ºC, 500hrs) 95 % - Initial Strength Retained for Ethanol (at 22ºC, 500hrs) 100 % - Initial Strength Retained for Motor Oil (at 125ºC, 500hrs) 95 % - Initial Strength Retained for Gasoline (at 22ºC, 500hrs) 100 % - Initial Strength Retained for Brake Fluid (at 22ºC, 500hrs) 100 % - Initial Strength Retained for Water/Glycol (at 87ºC, 500hrs) 90 % - Initial Strength Retained for Acetone (at 22ºC, 1000hrs) 95 % - Initial Strength Retained for Ethanol (at 22ºC, 1000hrs) 100 % - Initial Strength Retained for Motor Oil (at 125ºC, 1000hrs) 95 % - Initial Strength Retained for Gasoline (at 22ºC, 1000hrs) 100 % - Initial Strength Retained for Brake Fluid (at 22ºC, 1000hrs) 100 % - Initial Strength Retained for Water/Glycol (at 87ºC, 1000hrs) 85 % - - Cured Properties
Value Units Test Method / Conditions Handling Cure Time 30 minutes - Functional Cure Time 1 - 3 hrs - Full Cure Time 24 hrs - Breakaway Torque (M10 Steel Nuts and Bolts) 23 (200) N.m (lbs.in) ISO 10964 Prevail Torque (M10 Steel Nuts and Bolts) 25 (220) N.m (lbs.in) ISO 10964 Compressive Shear Strength of Steel Pins and Collars 14.5 (2102) N/mm² (psi) ISO 10123 Temperature Range -55 to 204 ºC - - Adhesive Properties
Value Units Test Method / Conditions Color Red - - Composition Methacrylate ester - - Viscosity (at 20 rpm, 25ºC, Brookfield RVT Spindle 3) 9500 cPs - Specific Gravity 1.12 - - Maximum Screw Size 1½ (36) inches (mm) - Flash Point min. 93 ºC - Solvent Content None - -
Safety & Health
- Precautions
This product and the auxiliary materials normally combined with it are capable of producing adverse health effects ranging from minor skin irritation to serious systemic effects. None of these materials should be used, stored, or transported until the handling precautions and recommendations as stated in the Material Safety Data Sheets (MSDS).
Storage & Handling
- Shelf Life
- 2 Years
- Storage Information
Anaerobic adhesives are ideally stored in a cool, dry place in unopened containers at a room temperature between 46°F to 82°F. Please do not return unused material to its original container.