- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress at Break at 23°C 120 MPa ISO 527-1/2 Tensile Stress at Break (23°C, 5mm/min) 120 MPa ISO 527-1/2 Tensile Strain at Break at 23°C 3 % ISO 527-1/2 Tensile Strain at Break (23°C, 5mm/min) 3 % ISO 527-1/2 Tensile Elastic modulus 23°C (1 mm/min) 9000 MPa ISO 527-1/2 Tensile Elastic Modulus (23°C, 1mm/min) 9000 MPa ISO 527-1/2 Izod Impact Strength Unnotched at 23°C 50 kJ/m2 ISO 180/1U Izod Impact Strength Unnotched (23°C) 50 kJ/m2 ISO 180/1U Izod Impact Strength Notched at 23°C 7 kJ/m2 ISO 180/1A Izod Impact Strength Notched (23°C) 7 kJ/m2 ISO 180/1A - Typical Properties
Value Units Test Method / Conditions Density at 23°C 1.53 g/cm3 ISO 1183 Density (23°C) 1.53 g/cm3 ISO 1183 Shrinkage - Parallel (115mm x 50mm x 3mm) 0.2 – 0.4 % Internal Shrinkage - Parallel (115mm x 50mm x 3mm) 0.2 - 0.4 % Internal Shrinkage - Normal (115mm x 50mm x 3mm) 0.8 – 1.2 % Internal Shrinkage - Normal (115mm x 50mm x 3mm) 0.8 - 1.2 % Internal Drying Temperature 120 °C - Drying Time 4 h - Melt Temperature 240 - 280 °C - Mould Temperature 80 – 120 °C - Mould Temperature 80 - 120 °C - - Thermal Properties
Value Units Test Method / Conditions VICAT Softening Point (50 N, 50°C/h) 205 °C ISO 306/B VICAT Softening Point (50N, 50°C/h) 205 °C ISO 306/B Heat Deflection Temperature (1,80 MPa - 120°C/h) 200 °C ISO 75-1/-2 Heat Deflection Temperature (1.80 MPa, 120°C/h) 200 °C ISO 75-1/-2 - Other Properties
Value Units Test Method / Conditions Burning Behaviour HB - UL94