Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Characterstics
- Very good impact/shock resistance
- High compressive strength
- Exceptional strength
- Good impact resistance
- Excellent cold flow behavior
- Approved for use in the food industry (EU and FDA)
- Capabilities
- Murylon® B White
- Rollers Slide bearings Parts subject to high impacts and shocks
Applications & Uses
Properties
- Mechanical Properties
Value Units Test Method / Conditions Breaking Elongation min. 50 % ISO 5271/2 Charpy Impact Strength o.B. kJ/m² ISO 1791/1eU Coefficient of Elasticity (Tensile Test) 3300 MPa ISO 5271/2 Coefficient of Sliding Friction (Dry)⁶ 0.35 μ - Indentation Hardness 150 N/mm² ISO 20391 Notch Impact Toughness (Charpy) 5.5 kJ/m² ISO 1791/1eA Pressure Test (Compression Strength at 1% Nominal Compression) 24 MPa ISO 604 Pressure Test (Compression Strength at 2% Nominal Compression) 46 MPa ISO 604 Pressure Test (Compression Strength at 5% Nominal Compression) 80 MPa ISO 604 Rockwell Hardness M85 - ISO 20392 Sliding Abrasion⁶ 0.23 μm/km - Time-dependent Creep Tensile Test (Stress Leading to an Elongation of 1% after 1000h) 18 MPa ISO 8991 Yield Stress 80 MPa ISO 5271/2 - Typical Properties
Value Units Test Method / Conditions Code PA 6 - ISO 10431 Material Colour Natural/ Black - - Density 1.14 g/cm ISO 11831 Water Absorption (After 24h Storage in Water at 23°C) 1.28 % ISO 62 Water Absorption (After 96h Storage in Water at 23°C) 2.5 % ISO 62 Water Absorption (Saturation in Standard Atmosphere of 23°C/50 % RH) 2.6 % - Water Absorption (Saturation in Water) 9 % - - Thermal Properties
Value Units Test Method / Conditions Burning behaviour as per UL94 (Sample thickness 3/6 mm) HB/HB - - Glass Transition Temperature 50 °C ISO 113571/2 Heat Conductivity (23°C) 0.28 W/(K x m) - Linear Thermal Coefficient of Expansion (Average Value between 23 and 100°C) 105 x 10⁻⁶ m/(K x m) - Linear Thermal Coefficient of Expansion (Average Value between 23 and 60°C) 90 x 10⁻⁶ m/(K x m) - Lower Service Temperature⁴ -40 °C - Melting Temperature 220 °C ISO 113571/3 Upper Service Temperature Constant in Air (20000h)³ 70 °C - Upper Service Temperature Constant in Air (5000h)³ 85 °C - Upper Service Temperature in Air (Short-term)² 160 °C - - Electrical Properties
Value Units Test Method / Conditions Specific Surface Resistance min. 10¹³ Ω IEC 60093 Dielectric Loss Factor (1 MHz) 21 - IEC 60250 Dielectric Loss Factor (100 Hz) 19 - IEC 60250 Electric Strength 25 kV/mm IEC 692431 Relative Permittivity (1 MHz) 3.3 - IEC 60250 Relative Permittivity (100 Hz) 3.9 - IEC 60250 Specific Contact Resistance min. 10⁻¹⁴ Ω x cm IEC 60093
Regulatory & Compliance
- Certifications & Compliance