Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
- Features
- Low VOC –JIS A-1901
- Low FOG - VDA278
- Aggressive acrylic adhesive
- Good shear properties
- Moisture stable PCK liner
- Benefits
- Acid free, PH Neutral
- Non-outgassing and non-migratory
- Smooth adhesive profile
- Excellent adhesion to a wide variety of surfaces.
- Chemical & UV resistant
- Excellent handling and die-cutting.
- Non-corrosive & non-oxidizing
Applications & Uses
- Markets
- Applications
- Compatible Substrates & Surfaces
- Applications
- Insulation and Shielding
- Wire harnessing
- Foam bonding applications
- Interior applications that require low vOC and low FOG characteristics
- Flexible Printed Circuits
- Printed Circuit Boards
- Archiving, photo mounting
- Application Details
For best performance surfaces must be clean, dry and free of any oil, grease or other contaminant.
Properties
- Physical Properties
Value Units Test Method / Conditions Total Thickness 7.8 mils - Loop Tack (stainless steel) 5.0 lbs./in. PSTC-16-Method A Peel Adhesion (180° 2 mil PET Backed 30minute dwell, stainless steel) 8.5 lbs./in. PSTC-101-Method A Peel Adhesion (180° 2 mil PET Backed 24hours dwell, stainless steel) 9.9 lbs./in. PSTC-101-Method A Peel Adhesion (180° 2 mil PET Backed 30minute dwell, ABS) 8.1 lbs./in. PSTC-101-Method A Peel Adhesion (180° 2 mil PET Backed 24minute dwell, ABS) 7.9 lbs./in. PSTC-101-Method A Peel Adhesion (180° 2 mil PET Backed 30minute dwell, Polycarbonate) 8.8 lbs./in. PSTC-101-Method A Peel Adhesion (180° 2 mil PET Backed 24minute dwell, Polycarbonate) 8.2 lbs./in. PSTC-101-Method A Peel Adhesion (180° 2 mil PET Backed 30minute dwell, HDPE) 2.9 lbs./in. PSTC-101-Method A Peel Adhesion (180° 2 mil PET Backed 24minute dwell, HDPE) 3.2 lbs./in. PSTC-101-Method A Peel Adhesion (180° 2 mil dead soft aluminum foil, 30minute dwell, stainless steel) 9.5 lbs./in. PSTC-101-Method A Peel Adhesion (180° 2 mil dead soft aluminum foil, 30minute dwell, Polypropylene) 3.0 lbs./in. PSTC-101-Method A Shear (1 kg weight, 72°F) min. 85 hours PSTC-107-Method A Formaldehyde Content 0.4 µ g/m3 JIS-A 1801 Acetaldehyde Content 1.2 µ g/m3 JIS-A 1801 Xylenes Content 1.4 µ g/m3 JIS-A 1801 Fog 30.0 µg/g VDA278 Fog 0.11 mg SAE J1756
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
- Certifications
- JIS A-1901
- ISO 18916
Technical Details & Test Data
- Product Construction
- Adhesive: 2.0 mils LV820 LOW VOC Acrylic
- Liner: 80# Natural PCK or 72# White PCK
- Web Width: 54”
- Service Temperature
- Application : Above 50°F (10°C) for best performance
- End Use : -40°F to 300°F (-40°C to 121°C) depending on laminate construction and end use application
- Foam Bonding Performance
Substrate Application Method Result EPDM Room Temp with 50% compression Foam Destruction
Nitrile PVCc Room Temp with 50% compression Foam Destruction
EVA Blend Room Temp with 50% compression Foam Destruction
Polyether polyurethane Foam Room Temp with 50% compression Foam Destruction
NBR-PVC Room Temp with 50% compression Foam Destruction
Storage & Handling
- Shelf Life
Two year shelf life when stored at 75°F. (24°C.) and 50% relative humidity or less. It is recommended that the product be stored in its original package until ready to use.