| Line Call Out | F712132B3E12K6M5 | - | ASTM F104 |
| Compressibility | 8 - 14 | % | ASTM F36J |
| Creep relaxation (1/32") | 20 | % | ASTM F38B |
| Density | 112 | lb/ft ³ (1.8 g/cc ³) | ASTM D149-95a |
| Dielectric Strength | 21 | kV/mm | ASTM D149-95a |
| Gas Permeability | max. 0.2 | ml/min | DIN 3535/6 |
| KLINGER Hot Compression Test Thickness Decrease 572°F (23°C) additional | 8 | % | - |
| KLINGER Hot Compression Test Thickness Decrease 73°F (23°C) initial | 12 | % | - |
| Leachable Chloride Content | 150 | ppm | FSA Method |
| Recovery | 50 | % | ASTM F36J |
| Sealability | max. 0.3 | ml/hr | ASTM F37A (1/32") |
| Thickness Increase ASTM F146 after immersion in ASTM Fuel A, 5h/73°F (23°C) | 0 - 4 | % | - |
| Thickness Increase ASTM F146 after immersion in ASTM Fuel B, 5h/73°F (23°C) | 0 - 5 | % | - |
| Thickness Increase ASTM F146 after immersion in ASTM Oil IRM 901, 5h/300°F (149°C) | 0 - 5 | % | - |
| Thickness Increase ASTM F146 after immersion in ASTM Oil IRM 903, 5h/300°F (149°C) | 0 - 7 | % | - |
| Weight increase ASTM F146 after immersion in Fuel B, 5h/73°F (23°C) | max. 10 | % | - |