| Elemendorf Tear Strength (MD) | 190 | g | ASTM D1922 |
| Elemendorf Tear Strength (TD) | 260 | g | ASTM D1922 |
| Film Toughness (MD) | 2220 | psi | ASTM D882 |
| Film Toughness (TD) | 1880 | psi | ASTM D882 |
| Tensile Elongation at Break (MD) | 510 | % | ASTM D882 |
| Tensile Elongation at Break (TD) | 640 | % | ASTM D882 |
| Tensile Strength at Break (MD) | 3930 | psi | ASTM D882 |
| Tensile Strength at Break (TD) | 2540 | psi | ASTM D882 |
| Tensile Strength at Yield (MD) | 1540 | psi | ASTM D882 |
| Tensile Strength at Yield (TD) | 1540 | - | - |
| Dart Drop Impact (1.0 mil) | 43 | g | ASTM D1709A |
| Density | 0.921 | g/cm³ | ASTM D 792 |
| Film Puncture Resistance (1.0mil) | 32 | ft-lb/in³ | - |
| Film Thickness - Tested | 1 | mil | - |
| Gloss (45°, 1 mil) | 92 | % | ASTM D2457 |
| Haze (1.0 mil) | 1.1 | % | ASTM D1003 |
| Melt Index (190°C/2.16 kg) | 7 | g/10 min | ASTM D1238 |
| Melting Temperature (DSC) | 230 / 110 | °F / °C | - |
| Vicat Softening Temperature | 192 / 88.9 | °F / °C | ASTM D1525 |