| Melt Index (190°C/2.16 kg) | 2 | g/10 min | ASTM D1238 |
| Brittleness Temperature | max. -105 (max. -76.1) | °F (°C) | ASTM D 746 |
| Deflection Temperature Under Load 66psi (0.45MPa) | 101 (38.3) | °F (°C) | ASTM D 648 |
| Density | 0.92 | g/cc | ASTM D 792 |
| Durometer Hardness | 45 | Shore D | ASTM D2240 |
| Environmental Stress-Cracking Resistance | 2 | hr | ASTM D1693 |
| Flexural Modulus - 2% Secant | 34,000 (234) | psi (MPa) | ASTM D 790 |
| Gloss (Blown Film) | 66 | - | ASTM D2457 |
| Gloss (Cast Film) | 75 | - | ASTM D2457 |
| Haze (Blown Film) | 0.076 | 2.00 mil | ASTM D1003 |
| Haze (Cast Film) | 0.048 | 1.00 mil | ASTM D1003 |
| Peak Crystallization Temperature (DSC) | 209 (98.3) | °F (°C) | - |
| Tensile Elongation at Break | 600 | % | ASTM D638 |
| Tensile Elongation at Yield | 4 | % | ASTM D638 |
| Tensile Impact Strength | 70 (147) | ft-lb/in² (kJ/m²) | ASTM D1822 |
| Tensile Strength at Break | 1600 (11) | psi (MPa) | ASTM D638 |
| Tensile Strength at Yield | 1300 (8.96) | psi (MPa) | ASTM D638 |
| Vicat Softening Temperature | 203 (95) | °F (°C) | ASTM D1525 |
| Vicat Softening Temperature | 233 (112) | °F (°C) | - |