| Thickness | 0.125 | inches | - |
| Tensile Strength (Lengthwise) | 58500 | psi | ASTMD638 |
| Tensile Strength (Crosswise) | 39000 | psi | ASTMD638 |
| Flexural Strength (Condition A, Lengthwise) | 84800 | psi | ASTMD790 |
| Flexural Strength (Condition A Crosswise) | 66100 | psi | ASTMD790 |
| Flexural Strength (D48/50, Lengthwise) | 80500 | psi | ASTMD790 |
| Flexural Strength (D48/50, Crosswise) | 60000 | psi | ASTMD790 |
| Compressive Strength (Lengthwise) | 43000 | psi | ASTMD695 |
| Compressive Strength (Crosswise) | 42200 | psi | ASTMD695 |
| Compressive Strength (Flatwise) | 48,500 + | psi | ASTMD256 |
| Notched Izod Impact (Condition A Lengthwise) | 15.9 | ft.lb./in. | ASTMD256 |
| Notched Izod Impact (Condition A Crosswise) | 9.7 | ft.lb./in. | ASTMD256 |
| Notched Izod Impact (D48/50 Lengthwise) | 15.4 | ft.lb./in. | ASTMD256 |
| Notched Izod Impact (D48/50 Crosswise) | 9.1 | ft.lb./in. | ASTMD256 |
| Notched Izod Impact (E48/50 Lengthwise) | 16.5 | ft.lb./in. | ASTMD256 |
| Notched Izod Impact (E48/50 Crosswise) | 9.6 | ft.lb./in. | ASTMD256 |
| Water Absorption (of weight) | 0.08 | % | ASTMD570 |
| Specific Gravity | 1.96 | - | ASTMD792 |
| U.L. Subject 94 | VO | - | ASTMUL94 |
| Dielectric Strength | 488 | Vpm | ASTMD149 |
| Dielectric Breakdown (Condition A) | 80+ | kV | ASTMD149 |
| Dielectric Breakdown (D48/50) | 45.2 | kV | ASTMD149 |
| Arc Resistance (Condition A) | 126 | seconds | ASTMD495 |
| Arc Resistance (D48/50) | 117 | seconds | ASTMD495 |
| Comparative Track Index (CTI) | 440 | Volts | U.L. 746A |
| U.L HV Track Rate | 2.2 | mm/Min. | U.L. 746A |
| Permittivity (1MHz, Condition A) | 4.79 | - | ASTMD150 |
| Permittivity (1MHz, D24/23) | 4.89 | - | ASTMD150 |
| Dissipation Factor, 1MHz (Condition A) | 0.016 | - | ASTMD150 |
| Dissipation Factor, 1MHz (D24/23) | 0.016 | - | ASTMD150 |
| Permittivity, 1KHz (Condition A) | 5.04 | - | ASTMD150 |
| Permittivity, 1KHz (D24/23) | 5.17 | - | ASTMD150 |
| Dissipation Factor, 1KHz (Condition A) | 0.005 | - | ASTMD150 |
| U.L. Hot Wire Ignition | 120+ | - | ASTMD150 |
| U.L. High Amp Ignition | 200 + | Exposure | U.L. 746A |
| Shear Strength | 21000 | psi | U.L. 746A |
| Thermal Conductivity (of thickness) | 7 x 10-4 | /calories per sec. /sq.cm /degree C/cm | - |
| Coefficient of Thermal Expansion | x 10-5 | cm/cm/°C | - |
| Youngs Modulus | 2500000 | psi | - |
| U.L. temperature Index (Electrical) | 130° C | - | - |
| U.L. temperure Index (Electrical) | 130 | °C | - |
| U.L. temperature Index (Mechanical) | 140° C | - | - |
| U.L. temperure Index (Mechanical) | 140 | °C | - |
| UL Listed | File #E37920 | - | - |
| Coefficient of Friction with semi gloss finish | ≈ .25 to .300 | - | - |