Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Mechanical Properties
Value Units Test Method / Conditions Charpy Notched Impact Strength (23°C) 4 kJ/m2 ISO 179/1eA Tensile Stress at Yield (50 mm/min) 36 MPa ISO 527-2 Charpy Unnotched Impact Strength (23°C) 52 kJ/m2 ISO 179 Tensile Modulus (1 mm/min) 2700 MPa ISO 527 Tensile Strain at Yield (50 mm/min) 2 % ISO 527-1,-2 Charpy Notched Impact Strength (-20°C) 2.4 kJ/m2 ISO 179/1eA Charpy Unnotched Impact Strength (-20°C) 42 kJ/m2 ISO 179/1eA Flexural Strength (2 mm/min) 64 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Density (23°C) 1.06 g/cm3 ISO 1183-1 Melt Flow Rate - MFR (200°C/5kg) 10 g/10 min ISO 1133 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature - HDT/A (1.8 MPa) 71 °C ISO 75-1,-2 - Processing Information (Extrusion)
Value Units Test Method / Conditions Recommended Processing Parameters Extrusion - - Barrel Temperatures 150 to 200 °C - Polymer Melt Temperature 150 to 220 °C - Die Temperature 150 to 200 °C - - Additional Information
Value Units Test Method / Conditions Abbreviated Term PS - ISO 1043