Properties
- Color
- Physical Form
- Physical Properties
Value Units Test Method / Conditions Density (23°C) 1.04 g/cm3 ISO 1183 Melt Mass Flow Rate - MFR (230°C/5kg) 0.8 g/10 min ISO 1133 - Mechanical Properties
Value Units Test Method / Conditions Tensile Strain at Yield (50 mm/min) 5.5 % ISO 527-2 Charpy Notched Impact Strength (-20°C) 2 kJ/m2 ISO 179/1eA Charpy Notched Impact Strength (23°C) 3.5 kJ/m2 ISO 179/1eA Charpy Impact Strength (23°C) 60 kJ/m2 ISO 179/1eU Tensile Stress at Yield (50 mm/min) 32 MPa ISO 527-2/1A Tensile Modulus (1 mm/min) 2500 MPa ISO 527 Flexural Modulus (2 mm/min) 2600 MPa ISO 178 Charpy Impact Strength (-20°C) 18 kJ/m2 ISO 179/1eU - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature - HDT/B (0.45 MPa) 115 °C ISO 75 - Processing Information (Extrusion)
Value Units Test Method / Conditions Recommended Processing Parameters Extrusion - - Barrel Temperatures 180 to 220 °C - Polymer Melt Temperature 200 to 230 °C - Die Temperature 190 to 220 °C - - Processing Information (Injection Molding)
Value Units Test Method / Conditions Recommended Processing Parameters Injection Molding - - Hold Pressure 50 – 100 % of actual injection pressure - - Mold Temperature 15 to 50 °C - Injection Speed Slow or Intermediate - - Barrel Temperatures 190 to 260 °C - Polymer Melt Temperature 240 to 260 °C - - Additional Information
Value Units Test Method / Conditions Abbreviated Term PPH TD20 - ISO 1043