Properties
- Physical Properties
Value Units Test Method / Conditions Mold Shrinkage - Cross Flow (-30°C) 43 x10-6mm/mm/°C TMA Mold Shrinkage - Flow (-30°C) 18 x10-6mm/mm/°C TMA Water Absorption (24h, 50% RH) 0.01 % ISO 62 Density 1.26 g/cm3 ISO 1183/A Glass Content 30 wt% - - Thermal Properties
Value Units Test Method / Conditions Linear Thermal Expansion Coefficient - Cross Flow 0.5 - 0.8 % Idemitsu Method Linear Thermal Expansion Coefficient - Flow 0.1 - 0.4 % Idemitsu Method Deflection Temperature Under Load (1.8 MPa) 250 - ISO 75 A Deflection Temperature Under Load (0.45 MPa) 270 - ISO 75 B - Electrical Properties
Value Units Test Method / Conditions Comparative Tracking Index - CTI 1 equivalent PLC level IEC 60112 Solution A Dielectric Constant (1 MHz) 2.9 - ASTM D 150 Dissipation Factor (1 MHz) max. 0.001 - IEC 60250 RTI Mechanical with Impact (Imp) 50 °C UL 746B RTI Mechanical Without Impact (Str) 50 °C UL 746B Dielectric Strength 45 kV/mm IEC 60243-1 RTI Elec 50 °C UL 746B Volume Resistivity min. 1E+16 Ω·cm ASTM D257 - Flammability
Value Units Test Method / Conditions Flammability 0.8-2.99 mm UL 94 - Processing Parameters
Value Units Test Method / Conditions Pre-drying Timings 3.0 - 5 h - Pre-drying Temperature 120 °C - Mold Temperature 130 - 155 °C - Melt Temperature 280 - 310 °C -