UL Flame Class Rating (File No. E88637) (C-UL CSA LS 103112) | HB | - | UL-94 |
Rockwell Hardness (23℃) | 104 | Scale R | D-785 |
Drying Temperature | 80 - 90 | (℃) | - |
Flexural Modulus (15mm/min. 1/8''×1''×4'') | 20800 | Kgf/cm2 | D-790 |
Flexural Strength (15mm/min. 1/8''×1''×4'') | 705 | Kgf/cm2 | D-790 |
Heat Deflection Temperature (Unannealed 18.6kg/cm2 (264 PSI) 1/2''×1/2''×5'') | 90 | ℃ | D-648 |
Injection Temperature | 170 - 240 | ℃ | - |
Izod Impact Strength (Notched 1/4) | 40 | Kgf-cm/cm. | D-256 |
Izod Impact Strength (Notched 1/8) | 57 | Kgf-cm/cm. | D-256 |
Melting Flow Rate (200℃/ 5㎏) | 0.8 | g/10min. | D-1238 |
Melting Flow Rate (220℃/10㎏) | 8 | g/10min. | ISO-1133 |
Mould Temperature | 40 - 80 | ℃ | - |
Specific Gravity | 1.03 | - | D-792 |
Tensile Strength (50mm/min. 1/8''thickness) | 425 | Kgf/cm2 | D-638 |