| UL Flame Class Rating (File No. E88637) (C-UL CSA LS 103112) | 5VA | - | UL-94 |
| Rockwell Hardness (23℃) | 105 | Scale R | D-785 |
| Drying Temperature | 75 - 85 | (℃) | - |
| Flexural Modulus (15mm/min. 1/8''×1''×4'') | 24500 | Kgf/cm2 | D-790 |
| Flexural Strength (15mm/min. 1/8''×1''×4'') | 710 | Kgf/cm2 | D-790 |
| Heat Deflection Temperature (Unannealed 18.6kg/cm2 (264 PSI) 1/2''×1/2''×5'') | 81 | ℃ | D-648 |
| Injection Temperature | 180 - 210 | ℃ | - |
| Izod Impact Strength (Notched 1/4) | 18 | Kgf-cm/cm. | D-256 |
| Izod Impact Strength (Notched 1/8) | 23 | Kgf-cm/cm. | D-256 |
| Melting Flow Rate (200℃/ 5㎏) | 6.3 | g/10min. | D-1238 |
| Melting Flow Rate (220℃/10㎏) | 6 | g/10min. | ISO-1133 |
| Mould Temperature | 40 - 80 | ℃ | - |
| Specific Gravity | 1.17 | - | D-792 |
| Tensile Strength (50mm/min. 1/8''thickness) | 430 | Kgf/cm2 | D-638 |