Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Recommended Applications
Suitable for high temperature applications, where higher strength & less coefficient of Friction in load-bearing applications. e.g. Valve Seats & Mechanical Seals is required. Chemically resistant to aggressive environments, suitable for valve sheet application in ball valves.
Properties
- Color
- Flame Rating
- Physical Form
- Mechanical Properties
Value Units Test Method / Conditions Flexural Strength 164 MPa ASTM D 790 Elongation at Break 2 % ASTM D 638 Flexural Modulus 4.1 GPa ASTM D 790 Izod Impact Strength(Notched) 45 J/m ASTM D 256 Izod Impact Strength(Un-notched) No Break J/m ASTM D 256 Tensile Modulus 5 - 8 GPa ASTM D 638 Tensile Strength 85 MPa ASTM D 638 - Thermal Properties
Value Units Test Method / Conditions Continuous Use Temperature ( Expected) 280 °C UL 746B Glass Transition Temperature (Tg) 152 °C ASTM D 3418 Melting Point (Tm) 372 °C ASTM D 3418 - Typical Properties
Value Units Test Method / Conditions Density at 23°C 1.4 g/cc - Mold Shrinkage (410°C nozzle, 220°C Mold) ( Across Flow) 1.9 % - Mold Shrinkage (410°C nozzle, 220°C Mold) ( Along Flow) 1.4 % - Water Absorption (24h, 23°C) 0.07 % ASTM D 570-98 - Flammability
Value Units Test Method / Conditions Flammability V-0 - UL 94/0.8 mm - Processing Parameters
Value Units Test Method / Conditions Drying Temperature at 150°C 4-6 hr - Hopper/ Throat Temperature 60-80 °C - Mold Temperature 200-220 °C - Nozzle Temperature 400 °C - Temperature Settings 390-400 °C -
Regulatory & Compliance
- Certifications & Compliance