Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Modulus 5000 - 5800 MPa ISO 527 - 2 Stress at Break 75.0 MPa ISO 527 - 2 Strain at Break 2.5 % ISO 527 - 2 Flexural Modulus 4800 - 5200 MPa ISO 178 Maximum Flexural Stress 120.0 MPa ISO 178 IZOD Notched Impact Strength (+23°C) 9.0 KJ/m2 ISO 180/1eA - Thermal Properties
Value Units Test Method / Conditions Heat Distortion Temperature (Under 1.8 Mpa Load, HDT A) 145.0 °C ISO 75 - 2 Vicat Softening Point (Under 0.49 N Load, Vicat B) 130.0 °C ISO 306 - Electrical Properties
Value Units Test Method / Conditions Volume Resistivity 100000000000000.0 Ω*cm IEC 60093 Surface Resistivity 1.0e+15 Ω IEC 60093 - Flammability
Value Units Test Method / Conditions Flammability Rate (0.8 mm thickness) HB - UL94 Flammability Rate (1.6 mm thickness) HB - UL94 Flammability Rate (3.2 mm thickness) HB - UL94 - Processing Parameters
Value Units Test Method / Conditions Melt Temperature 210-255 °C CYLINDER Mould Temperature 45-70 °C MOULD Drying Temperature 80.0 °C - Dry Time 2.0 h - - Rheological Properties
Value Units Test Method / Conditions Density 1.10 - 1.15 g/cm3 ISO 1183 Humidity Absorption 0.05 % Similar ISO 62 Melt Flow Index 4 - 7 cm3/10min ISO 1133 Molding Shrinkage (Parallel) 0.25 - 0.45 % ISO 294-4 Molding Shrinkage (Normal) 0.75 - 1.00 % ISO 294-4 Melting Point (DSC) 165.0 °C ISO 3146