Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Physical Properties
Value Units Test Method / Conditions Density (23°C) 1.52 g/cm3 ASTM D792 Water Adsorption (24h - 23°C) 0.1 % ASTM D570 Melt Flow Index (-20°C - 98 N) 15.0 g/10min. ASTM D1238 Linear Mould Shrinkage 0.3 - 0.5 % - - Mechanical Properties
Value Units Test Method / Conditions Tensile Strenght at Break (50 mm/min.) 130.0 MPa ASTM D638 Elongation At Break (50 mm/min.) 2.5 % ASTM D638 Bending Stress (1.3 mm/min.) 220.0 MPa ASTM D790 Flexural Modulus (1.3 mm/min.) 9000.0 MPa ASTM D790 Impact Strength (Notched (23°C - 3.2 mm) min. 80 J/m ASTM D256 Impact Strength (Notched (20°C - 3.2 mm) min. 50 J/m ASTM D256 Rockwell Hardness 90.0 Scala R ASTM D785 - Thermal Properties
Value Units Test Method / Conditions Heat Distortion Temperature (1.82 MPa) min. 200 °C ASTM D648 Vicat Softening Point (49N x 120°C/h) 220.0 °C ASTM D1525 Continuos Exercise Temperature (140h) 100.0 °C - - Electrical Properties
Value Units Test Method / Conditions Dielectric Costant (1MHz - secco) 3.8 - IEC 60250 Dielectric Strenght (S=1mm) 35.0 KV/mm IEC 60243-1 Volume Resistivity (Secco) min. 10^15 Ohm-cm IEC 60093 - Flammability
Value Units Test Method / Conditions Glow Wire Test (S=2 mm) 650.0 °C IEC 695-2-1 Flammability (S=1.6 mm) HB Classe UL 94 Flammability (S=3.2 mm) HB Classe UL 94 - Recommended Printing Conditions
Value Units Test Method / Conditions Cylinder Temperature 230 - 280 °C - Mold Temperature 60 - 90 °C - Dry Temperature (2-4 h) 90.0 °C - Injection Speed Medio-alta - -
Regulatory & Compliance
- Certifications & Compliance