Identification & Functionality
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Strength at Yield (50 mm/min.) 40.0 MPa ASTM D638 Elongation At Break (50 mm/min.) 30.0 % ASTM D638 Bending Stress (1.3 mm/min.) 65.0 MPa ASTM D790 Flexural Modulus (1.3 mm/min.) 2300.0 MPa ASTM D790 Impact Strength (Notched (23°C - 3.2 mm) min. 400 J/m ASTM D256 Impact Strength (Notched (20°C - 3.2 mm) min. 120 J/m ASTM D256 Rockwell Hardness 115.0 Scala R ASTM D785 - Physical Properties
Value Units Test Method / Conditions Density (23°C) 1.11 g/cm3 ASTM D792 Water Adsorption (24h - 23°C) 0.2 % ASTM D570 Melt Flow Index (-20°C - 98 N) min. 15 g/10min. ASTM D1238 Linear Mould Shrinkage 0.4 - 0.7 % - - Thermal Properties
Value Units Test Method / Conditions Heat Distortion Temperature (1.82 MPa) min. 90 °C ASTM D648 Vicat Softening Point (49N x 120°C/h) min. 110 °C ASTM D1525 Continuos Exercise Temperature 80.0 °C - - Electrical Properties
Value Units Test Method / Conditions Dielectric Costant (1MHz - secco) 2.9 - IEC 60250 Dielectric Strenght (S=1mm) 25.0 KV/mm IEC 60243-1 Volume Resistivity (Secco) min. 10^15 Ohm-cm IEC 60093 - Flammability
Value Units Test Method / Conditions Glow Wire Test (S=2 mm) 650.0 °C IEC 695-2-1 Flammability (S=1.6 mm) HB Classe UL 94 Flammability (S=3.2 mm) HB Classe UL 94 - Recommended Printing Conditions
Value Units Test Method / Conditions Cylinder Temperature 230 - 290 °C - Mold Temperature 70 - 90 °C - Dry Temperature (2-4 h) 90.0 °C - Injection Speed Medio-alta - -