Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Yield Stress 36 MPa ISO 527-1/-2 Yield Strain 17 % ISO 527-1/-2 Nominal Strain at Break >50 % ISO 527-1/-2 Charpy Notched Impact Strength (at +23°C) 10 kJ/m² ISO 179/1eA Charpy Notched Impact Strength (at -30°C) 6 kJ/m² ISO 179/1eA Izod Notched Impact Strength (at +23°C) 9 kJ/m² ISO 180/1A - Thermal Properties
Value Units Test Method / Conditions Melting Temperature (10°C/min) 221 °C ISO 11357-1/-3 Temperature of Deflection Under Load (0.45 MPa) 120 °C ISO 75-1/-2 Vicat Softening Temperature (50°C/h 50N) 160 °C ISO 306 Coefficient of Linear Thermal Expansion (parallel) 1.65 E-4/°C ISO 11359-1/-2 Coefficient of Linear Thermal Expansion (normal) 1.65 E-4/°C ISO 11359-1/-2 Burning Behaviour (at 1.5 mm Nominal Thickness) UL HB class IEC 60695-11-10 Glow Wire Ignition Temperature (at thickness 1 / - mm) 850 °C IEC 60695-2-13 Relative Temperature Index (Electrical, 1.5 mm) 50 °C UL746B Relative Temperature Index (with impact, 1.5 mm) 50 °C UL746B Relative Temperature Index (without impact, 1.5 mm) 50 °C UL746B - Electrical Properties
Value Units Test Method / Conditions Relative Permittivity (100Hz) 3.7 - IEC 62631-2-1 Relative Permittivity (1 MHz) 3.3 - IEC 62631-2-1 Dissipation Factor (1 MHz) 300 E-4 IEC 62631-2-1 Volume Resistivity 1E13 Ohm*m IEC 62631-3-1 Electric Strength 23 kV/mm IEC 60243-1 Comparative Tracking Index 600 V IEC 60112 - Rheological Calculation Properties
Value Units Test Method / Conditions Density of Melt 950 kg/m³ - Thermal Conductivity of Melt 0.1 W/(m K) - Specific Heat Capacity Melt 1900 J/(kg K) - Effective Thermal Diffusivity 5.54E-8 m²/s - - Other Properties
Value Units Test Method / Conditions Water Absorption 0.6 % Sim. to ISO 62 Humidity Absorption 0.15 % Sim. to ISO 62 Density 1290 kg/m³ ISO 1183 Apparent Density 830 kg/m³ ISO 60 - Mechanical Properties (TPE)
Value Units Test Method / Conditions Tensile Modulus 800 MPa ISO 527-1/-2 Stress at 5% strain 30 MPa ISO 527-1/-2 Stress at 10% strain 34 MPa ISO 527-1/-2 Stress at 50% strain 25 MPa ISO 527-1/-2 Stress at 100% strain 26 MPa ISO 527-1/-2 Stress at Break 43 MPa ISO 527-1/-2 Strain at Break 250 % ISO 527-1/-2 Nominal Strain at Break 360 % ISO 527-1/-2 Compression Set Under Constant Strain (at 70°C) 35 % ISO 815 Tear Strength 215 kN/m ISO 34-1; Method B Shore D Hardness (3s) 70 - ISO 868 - Rheological Properties
Value Units Test Method / Conditions Melt Volume-Flow Rate (at 230 / * °C, 2.16 / * kg) 18 cm³/10min ISO 1133 Molding Shrinkage (parallel) 1.75 % Sim. to ISO 294-4 Molding Shrinkage (normal) 2 % Sim. to ISO 294-4
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
Technical Details & Test Data
- Creep Modulus-Time 23°C
- Chemical Resistance
Chemical Type Chemical Name Resistance Other Acetic acid (10% by mass) at 23°C resistant Ketones Acetone at 23°C resistant Other Ammonium hydroxide (10% by mass) at 23°C limited resistant, tests necessary to verify Other ASTM 1 at 23°C resistant Other ASTM 3 at 23°C resistant Other Brake fluids (DOT 3/4) at 23°C not resistant Other Calcium chloride (10% by mass) at 23°C limited resistant, tests necessary to verify Other Chloroform at 23°C not resistant Ethers Diethyl ether at 23°C limited resistant, tests necessary to verify Alcohols Ethanol at 23°C limited resistant, tests necessary to verify Other Ethyl Acetate at 23°C limited resistant, tests necessary to verify Other Fuel; Diesel at 85°C resistant Other Hydrochloric acid (10% by mass) at 23°C resistant Other Hydrogen peroxide (30% by mass) at 23°C limited resistant, tests necessary to verify Other Nitric acid (10% by mass) at 23°C resistant Other Phosphoric acid (10% by mass) at 23°C resistant Other Sodium hydroxide (10% by mass) at 23°C resistant Other Sulfuric acid (30% by mass) at 23°C resistant Other Tetrachloroethylene at 23°C limited resistant, tests necessary to verify Hydrocarbons Toluene at 23°C resistant Other Transformer oil at 23°C not resistant Other Trichloroethylene at 23°C not resistant Other Water at 23°C resistant Other Zinc chloride (10% by mass) at 23°C resistant - Creep Modulus-Time 60°C
- Dynamic Shear Modulus (G)-Temperature
- Dynamic Tensile Modulus (E)-Temperature
- Shearstress-Shear Rate
- Specific Volume-Temperature (pvT)
- Stress-Strain
- Stress-Strain (TPE)
- Viscosity-Shear Rate