Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Strength at Yield 159 MPa ASTM D638 Tensile Strength at Break 155 MPa ASTM D 638 Tensile Elongation at Break 3 - ASTM D412 Flexural Strength 186 MPa ASTM D 790 Flexural Modulus 9655 MPa ASTM D790 Izod Notched Impact Strength (73°F) 80 J/m ASTM D256 - Physical Properties
Value Units Test Method / Conditions Molding Shrinkage - Flow (0.126 in (3.20 mm)) 0.001 - 0.002 mm/mm ASTM D955 Specific Gravity 1.52 - - Filler Content 40 % SABIC method - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature - HDT (264 psi) 146 °C ASTM D648 Heat Deflection Temperature - HDT (66 psi) 152 °C ASTM D648 - Processing Information (Injection Molding)
Value Units Test Method / Conditions Drying Temperature 200 - 250 °F - Drying Time 4 hr - Maximum Drying Time 7 h - Melt (processing) Temperatures 590 - 630 °F - Suggested Maximum Moisture 0.2 % - Suggested Shot Size 40 - 75 % - Rear Barrel Temperatures 550 - 590 °F - Middle Barrel Temperatures 570 - 610 °F - Front Barrel Temperatures 590 - 630 °F - Nozzle Temperature 580 - 620 °F - Back Pressure 50 - 100 psi - Mold Temperatures 180 - 240 °F - Screw speed 25 - 75 rpm - Vent Depth 0.0015 - 0.0030 in -