Properties
- Color
- Flame Rating
- Physical Form
- Flame Rating
- UL 94 HB
- Mechanical Properties
Value Units Test Method / Conditions Tensile Modulus (23°C/50% Relative Humidity, 5 mm/min) 290000 psi ASTM D 638 Tensile Modulus (23°C/50% Relative Humidity, 1 mm/min) 2000 MPa ISO 527-1,2 Yield Stress (23°C/50% Relative Humidity, 5 mm/min) 39 MPa ASTM D 638 Yield Stress (23°C/50% Relative Humidity, 50 mm/min) 42 MPa ISO 527-1,2 Strain at Break (23°C/50% Relative Humidity, 5 mm/min) 53 % ASTM D 638 Strain at Yield (23°C/50% Relative Humidity, 5mm/min) 7 % ISO 527-1,2 Strain at Break (23°C/50% Relative Humidity, 50 mm/min) 53 % ISO 527-1,2 Flexural Strength (23°C/50% Relative Humidity, 2 mm/min) 68 MPa ISO 178 Flexural Modulus (23°C/50% Relative Humidity, 1.3 mm/min) 290000 psi ASTM D 790 Flexural Modulus (23°C/50% Relative Humidity, 2 mm/min) 2000 MPa ISO 178 Charpy Notched Impact Strength (-22°F (-30°C), 50% Relative Humidity) 40 kJ/m2 ISO 179-1eA Charpy Notched Impact Strength (23°C (73°F), 50% Relative Humidity) 53 kJ/m2 ISO 179-1eA Izod Notched Impact Strength (-22°F (-30°C), 50% Relative Humidity, 3.2mm, 1/8”) 505 J/m ASTM D 256 Izod Notched Impact Strength (73°F (23°C), 50% Relative Humidity, 3.2mm, 1/8”) 780 J/m ASTM D 256 Izod Notched Impact Strength (73°F (23°C), 50% Relative Humidity, 6.4mm,1/4”) 565 J/m ASTM D 256 Izod Notched Impact Strength (23°C (73°F), 50% Relative Humidity) 58 kJ/m2 ISO 180-1A Izod Notched Impact Strength (-30°C (-22°F), 50% Relative Humidity) 41 kJ/m2 ISO 180-1A Ball Indentation Hardness (23°C/50% Relative Humidity) 90 N/mm2 ISO 2039-1 - Physical Properties
Value Units Test Method / Conditions Melt Flow Rate - MFR (230°C, 3.8Kg) 3 g/10min ASTM D1238 Melt Volume Flow Rate - MVFR (260°C, 5Kg) 14 cm3/10min ISO 1133 Molding Shrinkage - Normal (60X60X2 mm) 0.65-0.75 % ISO 294-4 Molding Shrinkage - Parallel (60X60X2 mm) 0.65-0.75 % ISO 294-4 Density (25°C) 1.07 g/cm3 ISO 1183-1 - Thermal Properties
Value Units Test Method / Conditions Coefficient Of Linear Thermal Expansion - Parallel (23 to 55°C) 0.89 10-4/K ISO 11359 -1,2 Deflection Temperature Under Load (0.45 Mpa) 113 °C ISO 75-1,2 Deflection Temperature Under Load (1.80 Mpa) 101 °C ISO 75-1,2 Vicat Softening Temperature (50N, 50°C/h) 235 ºF ASTM D 1525 Vicat Softening Temperature (B120, 120°C/h) 115 °C ISO 306 Vicat Softening Temperature (B50, 50°C/h) 113 °C ISO 306 - Flammability
Value Units Test Method / Conditions Burning Behavior (1.6 mm) HB Class - UL 94 Burning Behavior (1.6 mm) HB Class UL 94 Burning Rate (US-FMVSS, 200X105X2mm) max. 40 mm/min ISO 3795 - Processing Information (Injection Molding)
Value Units Test Method / Conditions Mold Temperature 70 °C ISO 294 Injection Velocity 240 mm/s ISO 294 Melt Temperature 240 °C ISO 294