Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Key Attributes
- Recycled material used in the formulation
- Reduced carbon footprint
- Equivalent properties to prime version
- High impact
- Low emission grade
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Form
- Mechanical Properties
Value Units Test Method / Conditions Yield Stress (at 50mm/min) 42.0 MPa ISO 527-1,2 Yield Strain (at 50mm/min) 3,0 % ISO 527-1,2 Elongation at Break (at 50 mm/min) 28.0 % ISO 527-1,2 Tensile Modulus (at 1mm/min) 2000.0 MPa ISO 527-1,-2 Flexural Modulus (at 2 mm/min) 2100.0 MPa ISO 178 Flexural Strength (at 2 mm/min) 68.0 MPa ISO 178 Izod Notched Impact Strength (at 23°C) 33.0 kJ/m² ISO 180-1A Charpy Notched Impact Strength (at 23°C) 31.0 kJ/m² ISO 179-1eA Charpy Notched Impact Strength (at -30°C) 22.0 kJ/m² ISO 179-1eA - Thermal Properties
Value Units Test Method / Conditions Vicat Softening Temperature (at 50B, 50ºC/h) 102.0 ºC ISO 306 Deflection Temperature Under Load (at 0.45 MPa) 104.0 ºC ISO 75-1,2 Coefficient of Linear Thermal Expansion (Parallel, 23 - 55°C) 0.9 10-^{4} /K ISO 11359 -1,2 Coefficient of Linear Thermal Expansion (Transverse, 23 - 55°C) 0.9 10-^{4} /K ISO 11359 -1,2 Burning Rate (US-FMVSS, 150x105x2 mm) max. 80 mm/min ISO 3795 - Typical Properties
Value Units Test Method / Conditions Density 1.07 g/cm³ ISO 1183 - Processing Information (Injection Molding)
Value Units Test Method / Conditions Injection Molding-Melt Temperature 240.0 ºC ISO 294 Injection Molding-Mold Temperature 70.0 ºC ISO 294 Injection Molding-Injection Velocity 240.0 mm/s ISO 294 - Rheological Properties
Value Units Test Method / Conditions Melt Volume-Flow Rate (at 260°C, 5Kg) 18.0 cm³/(10 min) ISO 1133