Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Physical Form
- Flame Rating
- UL 94 HB
- Mechanical Properties
Value Units Test Method / Conditions Tensile Modulus (23°C/50% Relative Humidity, 5 mm/min) 290000 psi ASTM D 638 Tensile Modulus (23°C/50% Relative Humidity, 1 mm/min) 2000 MPa ISO 527-1,2 Yield Stress (23°C/50% Relative Humidity, 5 mm/min) 42 MPa ASTM D 638 Tensile Stress at Break (23°C/50% Relative Humidity, 50 mm/min) 37 MPa ISO 527-1,2 Yield Stress (23°C/50% Relative Humidity, 50 mm/min) 45 MPa ISO 527-1,2 Tensile Strain at Break (23°C/50% Relative Humidity, 5 mm/min) 30 % ASTM D 638 Nominal Strain at Break (23°C/50% Relative Humidity, 50 mm/min) 15 % ISO 527-1, -2 Yield Strain (23°C/50% Relative Humidity, 50 mm/min) 3.7 % ISO 527-1, -2 Tensile Strain at Break (23°C/50% Relative Humidity, 50 mm/min) 30 % ISO 527-1,2 Flexural Strength (23°C/50% Relative Humidity, 2 mm/min) 70 MPa ISO 178 Flexural Modulus (23°C/50% Relative Humidity, 1.3 mm/min) 290000 psi ASTM D 790 Flexural Modulus (23°C/50% Relative Humidity, 2 mm/min) 2000 MPa ISO 178 Charpy Notched Impact Strength (23°C (73°F), 50% Relative Humidity) 40 kJ/m2 ISO 179-1eA Charpy Notched Impact Strength (-30°C (-22°F), 50% Relative Humidity) 30 kJ/m2 ISO 179-1eA Izod Notched Impact Strength (-22°F (-30°C), 50% Relative Humidity, 3.2mm, 1/8”) 275 J/m ASTM D 256 Izod Notched Impact Strength (73°F (23°C), 50% Relative Humidity, 3.2mm, 1/8”) 570 J/m ASTM D 256 Izod Notched Impact Strength (73°F (23°C), 50% Relative Humidity, 6.4mm,1/4”) 395 J/m ASTM D 256 Izod Notched Impact Strength (23°C (73°F), 50% Relative Humidity) 42 kJ/m2 ISO 180-1A Izod Notched Impact Strength (-30°C (-22°F), 50% Relative Humidity) 34 kJ/m2 ISO 180-1A Ball Indentation Hardness (23°C/50% Relative Humidity) 85 N/mm2 ISO 2039-1 - Physical Properties
Value Units Test Method / Conditions Melt Flow Rate - MFR (230°C, 3.8 Kg) 4 g/10min ASTM D1238 Melt Volume Flow Rate - MVFR (260°C, 5 Kg) 14 cm3/10min ISO 1133 Molding Shrinkage - Normal (150X105X3 mm) 0.6-0.8 % ISO 294-4 Molding Shrinkage - Parallel (150X105X3 mm) 0.6-0.8 % ISO 294-4 Density (25°C) 1.07 g/cm3 ISO 1183-1 - Thermal Properties
Value Units Test Method / Conditions Coefficient Of Linear Thermal Expansion - Parallel (23 to 55°C) 0.9 10-4/K ISO 11359 -1,2 Coefficient Of Linear Thermal Expansion - Transverse (23 to 55°C) 0.9 10-4/K ISO 11359 -1,2 Deflection Temperature Under Load (0.45 Mpa) 108 °C ISO 75-1,2 Deflection Temperature Under Load (1.80 Mpa) 99 °C ISO 75-1,2 Vicat Softening Temperature (50N, 50°C/h) 223 ºF ASTM D 1525 Vicat Softening Temperature (B50, 50°C/h) 106 °C ISO 306 - Electrical Properties
Value Units Test Method / Conditions Relative Permittivity (23°C/50 % Relative Humidity, 100 Hz) 3 - IEC 60250 Dissipation Factor (23°C/50 % Relative Humidity, 1 MHz) 86 10-4 IEC 60250 Dissipation Factor (23°C/50 % Relative Humidity, 100 Hz) 38 10-4 IEC 60250 Volume Resistivity (23°C/50 % Relative Humidity) 600000000000000 Ohm·m IEC 60093 Surface Resistivity (23°C/50 % Relative Humidity) 2E17 Ohm IEC 60093 - Flammability
Value Units Test Method / Conditions Burning Rate (US-FMVSS, 200X105X2mm) 34 mm/min ISO 3795 Burning Behavior (1.6 mm) HB Class - UL 94 Burning Behavior (1.6 mm) HB Class UL 94 Glow Wire Test - GWFI (2.0 mm) 700 °C IEC 60695-2-12 - Processing Information (Injection Molding)
Value Units Test Method / Conditions Mold Temperature 70 °C ISO 294 Injection Velocity 240 mm/s ISO 294 Melt Temperature 240 °C ISO 294