A versatile ABS (acrylonitrile butadien styrene) resin.
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
Properties
- Flame Rating
- Physical Properties
Value Units Test Method / Conditions Melt Mass Flow Rate (220°C 98N) 22 g/10min ISO 1133 Tensile Modulus (1mm/min) 2450 MPa ISO 527-1, -2 Tensile Stress at Yield (50mm/min) 47 MPa ISO 527-1, -2 Tensile Stress at Break (50mm/min) 35 MPa ISO 527-1, -2 Flexural Modulus (2mm/min) 2300 MPa ISO 178 Flexural Strength (2mm/min) 74 MPa ISO 178 Charpy Impact Strength Notched 21 kJ/m2 ISO 179 Temperature of Deflection (under load 1.8MPa Flatwise) 79 °C ISO 75-1, -2 Vicat Softening Temperature (50N) 101 °C ISO 306 Vicat Softening Temperature (50N) 100 °C ASTM D-1525 Rockwell Hardness R-scale 109 - ISO 2039-2 Rockwell Hardness R-scale 116 - ASTM D-785 Density (23°C) 1050 kg/m3 ISO 1183 Density (23°C) 1.04 - ASTM D-792 Tensile Modulus 45 MPa ASTM D-638 Flexural Modulus (15mm/min) 2400 MPa ASTM D-790 Flexural Strength (15mm/min) 72 MPa ASTM D-790 Izod Impact Strength Notched 226 J/m ASTM D-256 Heat Deflection Temperature (1.8MPa Edgewise) 89 °C ASTM D-648 Flammability HB - UL94 Molding Shrinkage (2mmt) 0.4～0.6 % DENKA Method Surface Resistivity (23°C,50%RH) min. 10¹⁶ Ω JIS K 6911
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Processing Condition and Molding Condition
Pre-drying Condition
Temperature [°C] Time [hr] 80～85 2～3 Molding Condition
Cylinder temperature setting [°C] Grade C1 C2 C3 Nozzle QF, GT-R-61A 170 180 190 190 ～ ～ ～ ～ 190 215 230 225 180 190 200 200 GS-10, GR-0500, GR-1000, GT-R-10 ～ ～ ～ ～ 200 220 240 235 180 200 210 210 GR-2000, GR-3000, ME, GR-3500,GR-2000LG, APG-3000～ ～ ～ ～ 200 230 260 255 Mold temperature: 40～60 [°C] (actual temperature of mold surface)
Screw rotation speed: 80～120 [rpm]
Back pressure: 5～10 [kg/cm2・G]