Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
- Suitable Lamp Types
LED 400 nm, LED 460 nm, UVA
Features & Benefits
- Ready-to-Use Product Features
- Special Features
- compliant with RoHS Directive 2015/863/EU
- passes ANSI/UL 94 HB Flame Test
- Function
- electronic adhesive
- electronic encapsulant
Applications & Uses
- Markets
- Applications
- Typical Area Of Use
- -40 - 150 °C
- bonding of opaque components
- pin sealing
- General Curing and Processing Information
The curing time stated in the technical data was determined in the laboratory. It can vary depending on the adhesive quantity and component geometry and is therefore a reference value.
Increasing or decreasing the curing temperature and / or irradiation intensity and / or irradiation time shortens or prolongs the curing time and can lead to changed physical properties.
A short irradiation time (preactivation time) results in an open time within which opaque components can be joined.
The cationic curing mechanism enables the adhesive to cure on opaque components after joining by sufficient preactivation.
All curing or light fixation parameters depend on material thickness and absorption, adhesive layer thickness, lamp type and distance between lamp and adhesive layer.
Curing until final strength proceeds within 24 hours at room temperature.
High temperatures during or after curing can lead to post-crosslinking of the adhesive which influences the physical properties of the bond.
Values measured after 24 h at approx. 23 °C / 50 % r.h., unless otherwise specified.
Properties
- Typical Properties
Value Units Test Method / Conditions Typical Preactivation Time Intensity 200 Mw/Cm² Led 460 Nm 3.0 s - Typical Open Time Intensity 200 Mw/Cm² Led 460 Nm 16 - 21 s - Typical Irradiation Time Intensity 200 Mw/Cm² Led 400 Nm 40 - 60 s - Color In Cured Condition In 0.1 Mm Layer Thickness Yellow - - Transparency In Cured Condition In 0.1 Mm Layer Thickness Transparent - - - Processing Parameters
Value Units Test Method / Conditions Density 1.1 g/cm³ DIN EN ISO 2811-3 Viscosity Rheometer | Shear Rate: 10 1/S 1200.0 mPa·s - Maximum Layer Thickness That Can Be Preactivated Delo Standard 21 | Preactivation | 460 Nm | 200 Mw/Cm² | 3 S | Plus | At Approx. +23 °C | 24 H min. 4 mm - Compression Shear Strength Delo Standard 5 | Glass | Glass | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H min. 20 MPa - Compression Shear Strength (Delo Standard 5 | Glass | Lcp Gf30 | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H) 7.0 MPa - Compression Shear Strength (Delo Standard 5 | Pc | Pc | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H) 37.0 MPa - Compression Shear Strength (Delo Standard 5 | Pc | Al | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H) 6.0 MPa - Compression Shear Strength (Delo Standard 5 | Glass | Al | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H) min. 20 MPa - Compression Shear Strength (Delo Standard 5 | Glass | Pbt | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H) 15.0 MPa - Compression Shear Strength Delo Standard 5 | Glass | Fr4 | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H min. 20 MPa - Tensile Strength 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H 33.0 MPa DIN EN ISO 527 Elongation At Tear | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H 5.7 % DIN EN ISO 527 Young'S Modulus Dmta | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H | Type Of Storage: Temp. | Storage Temperature: 205 °C | Duration: 30 Min 1800.0 MPa DMTA EN ISO 400 Shore Hardness D (400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H) 67.0 - DIN EN ISO 868 Glass Transition Temperature Dmta | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H | Type Of Storage: Temp. | Storage Temperature: 205 °C | Duration: 30 Min 153.0 °C - Coefficient Of Linear Expansion (Delo Standard 26 | Tma | Evaluation T: 40 °C - 55 °C | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H) 120.0 ppm/K - Coefficient Of Linear Expansion (Delo Standard 26 | Tma | Evaluation T: 130 °C - 160 °C | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H) 173.0 ppm/K - Shrinkage Delo Standard 13 | 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H 4.3 vol. % - Water Absorption Based On 400 Nm | 200 Mw/Cm² | 60 S | Plus | At Approx. +23 °C | 24 H | Type Of Storage: Media | Medium: Distilled Water | Duration: 24 H 1.0 wt. % DIN EN ISO 62 Creep Resistance Cti M Based On | 60 Mw/Cm² | 120 S | Plus | At Approx. +23 °C | 24 H min. 600 - DIN EN 60112
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Converting Table
°F = (°C *1.8) +32
1 inch = 25.4 mm
1 mil = 25.4
1 oz = 28.3495 g
1 MPa = 145.04 psi
1 GPa = 145.04 ksi
1cP = 1 mPa•s
IN = 0.225 lb
Storage & Handling
- Storage Life
In Unopened Original Container (at 0 °C To +25 °C) is 6 months