Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Carrier
- Chemical Family
- CASE Ingredients Functions
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- CASE Ingredients Features
- Materials Features
Applications & Uses
- Markets
- Applications
- Compatible Polymers & Resins
- Compatible Substrates & Surfaces
- Cure Method
- Coating Type
- Plastics & Elastomers End Uses
- Application
(1) Coatings: Recommended for enhancing adhesion of UV/ EB cured coatings, ie acrylic, etc. to metal surfaces with resultant reduction in corrosion. Enhances adhesion to many plastic surfaces (oxygen containing polymers only) or treated polyolefins.
(2) Adhesives/ Sealants: Recommended for acrylate/ methacrylate adhesives and sealants for improved adhesion to metals, concrete, wood, many plastics (oxygen containing polymers only) and ceramics. Improved T-peel strength and resistance to moisture. Not recommended for adhesion to glass.
(3) Rubber: Improved physical properties in mineral filled silicone, EPDM and other peroxide cured rubbers.
(4) Plastics: Improved physical properties in free radical cured resins, ie polyesters, acrylics, and polyurethanes.
Properties
- Physical Form
- Physical Properties
Value Units Test Method / Conditions Active Matter Content 23 wt% - Complexed Organics 9.1 - 9.3 - - Specific Gravity 1.15 g/ml - Total Metal Content 5.2 - 5.9 % - Organofunctionality Methacrylato - - pH Value (2% Solution) 3.9 - -
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
Technical Details & Test Data
- Procedure
- HIGH SHEAR MIXING NECESSARY IN ALL SOLVENT-BORNE SYSTEMS
(1) Coatings/ Inks: Optimum performance is achieved when added directly to the grind stage resin and high shear mixed for 15 mins before adding other components. Must be high shear mixed with a Cowles type mixer. Milling alone is not sufficient.
(2) Adhesives: 1.0-2.0 phr, post add recommended under agitation.
(3) Plastics: 1.0-2.0 phf (parts per hundred filler); recommend pretreat of pigments/ fillers in a Henschel or similar mixer and subsequently compound with resin. For high surface area pigments/ fillers, i.e. fumed silica, carbon black, phthalo, and similar use 3.0-5.0 phf.
(4) Rubber: 1.0-3.0 phr, add directly onto silica or other filler and compound in a Banbury mixer.