| Tensile Strength at Yield (Type V, 1 mm/min, UV Cured) | 46 ± 3 | MPa | ASTM D638 |
| Ultimate Tensile Strength (Green State, Type V, 10 mm/min) | 25 ± 2 | MPa | ASTM D638 |
| Ultimate Tensile Strength (UV Cured, Type V, 1 mm/min) | 46 ± 3 | MPa | ASTM D638 |
| Tensile Modulus (Green State, Type V, 10 mm/min) | 731 ± 120 | MPa | ASTM D638 |
| Tensile Modulus (UV Cured, Type V, 1 mm/min) | 2000 ± 100 | MPa | ASTM D638 |
| Elongation at Break (Green State, Type V, 10 mm/min) | 33 ± 2 | % | ASTM D638 |
| Tensile Strain at Yield (UV Cured, Type V, 10 mm/min) | 5.7 ± 0.2 | % | ASTM D638 |
| Flexural Modulus (chord, 0.5-1 % strain, UV Cured) | 2010 ± 119 | MPa | ASTM D790-B |
| Izod Notched Impact Strength (Machined, UV Cured) | 33 ± 4 | J/m | ASTM D256 |
| Izod Unnotched Impact Strength Impact Strength (UV Cured) | 496 ± 141 | J/m | ASTM D4812 |