Cactus Industrial PMMA-Based Anti Slip Paint

• Fast-curing with a hardening time of just 40 minutes at 20°C and with a PMMA Catalyst dosage of 2% pbw. added to the Resin Base
• A tough and durable coating with excellent grip properties.
• Choices of fine, medium and coarse aggregate are available.
• Suitable for internal and external application, including in wet environments.
• Excellent resistance to UV and weathering.
• Good chemical resistance.
• Can be applied in temperatures as low as 0°C to 30°C.

• Walkways
• Production Areas
• Warehouse
• Car Parking
• Offshore decks, lay down areas and walkways
• Balcony Waterproofing

• For Mixing the Product: Twin paddle mixer, steel container.
• Method of application: Brush, roller. The aggregate is then evenly broadcast across the material upon application.
• Thinner: Do not thin.
• Cleaner: PMMA cleaning agent 10 liter.

• Ensure all areas are clean, dry and free from dust, dirt, corrosion and general surface contamination.
• All oils, grease, etc. should be removed with suitable degreasing solution pre application onto any pre-applied PMMA.
• Concrete and steel surfaces should be preferably Bristle Blasted/Grit blasted to SA 2½ in accordance with DIN 55929.
• Non-ferrous metals must be cleaned and prepared by Bristle Blasting or Grit blasting.
• Always prime the substrate.

• Due to exothermic reaction with mixing process, please ensure the product is mixed in a steel container.
• First stir the PMMA-Based Waterproofing liquid Coating with a paddle mixer thoroughly.
• Then add the PMMA Catalyst while stirring the waterproofing liquid coating at a slow speed.
• Mix for 1 - 2 minutes.
• You must not dose less than the given quantity of PMMA Catalyst, as this will jeopardize the curing process.
• You must also avoid overdosing the PMMA Catalyst, as this can likewise lead to serious curing problems.
• The material must be applied as soon as the PMMA Catalyst has finished dissolving in the resin components.
• The fine, medium or coarse aggregate is then evenly broadcast across the material upon application.

• If work is interrupted or when it is completed, clean the tools thoroughly with cleaning agent within the pot life of the material.
• This can be done with a brush.
• Do not use the tools again until the cleaning agent has evaporated fully.
• Simply immersing the tools in the cleaning agent will not prevent the material from hardening.

Practical coverage can vary considerably depending on method of application, surface roughness, weather conditions and complexity of the structure.

0.6 - 1.1 kg/m².

0 - 30 °C