- Physical Form
- Typical Properties
Value Units Test Method / Conditions C14 Content min. 87 % ASTM D 6866 - Blown Film Properties
Value Units Test Method / Conditions Tensile Strength (at Break, MD) 50.0 MPa ASTM D882 Tensile Strength (at Break, TD) 40.0 MPa ASTM D882 Elongation (at Break, MD) 1130.0 % ASTM D882 Elongation (at Break, TD) 1430.0 % ASTM D882 Tensile Modulus (1% Secant, MD) 180.0 MPa ASTM D882 Tensile Modulus (1% Secant, TD) 200.0 MPa ASTM D882 Dart Drop Impact Strength 120.0 g/F50 ASTM D1709 Elmendorf Tear Strength (MD) 180.0 gF ASTM D1922 Elmendorf Tear Strength (TD) 400.0 gF ASTM D1922 Haze 12.0 % ASTM D1003 Gloss (Angle 60°) 48.0 % ASTM D2457 - Control Properties
Value Units Test Method / Conditions Melt Flow Rate (at 190°C, 2.16kg) 1.0 g/10 min ASTM D1238 Density 0.916 g/cm³ ASTM D1505 - Note
Blown Film Properties:
- LDPE: 100 μm thick film, obtained from a 40 mm extruder, with blow up ratio of 2.2:1 (MD = Machine Direction and TD = Transversal Direction).