Properties
- Physical Form
- Typical Properties
Value Units Test Method / Conditions C14 Content min. 96 % ASTM D 6866 - Control Properties
Value Units Test Method / Conditions Melt Flow Rate (at 190°C, 5kg) 0.33 g/10 min ASTM D 1238 Melt Flow Rate (at 190°C, 21.6kg) 9.3 g/10 min ASTM D1238 Density 0.952 g/cm³ ASTM D792 - Typical Properties - Blown Film Properties
Value Units Test Method / Conditions Tensile Strength (at Break, MD) 85.0 MPa ASTM D882 Tensile Strength (at Break, TD) 45.0 MPa ASTM D882 Elongation (at Break, MD) 590.0 % ASTM D882 Elongation (at Break, TD) 740.0 % ASTM D882 Tensile Strength (at Yield, MD) 40.0 MPa ASTM D882 Tensile Strength (at Yield, TD) 30.0 MPa ASTM D882 Elongation (at Yield, MD) 15.0 % ASTM D882 Elongation (at Yield, TD) 5.0 % ASTM D882 Dart Drop Impact Strength 200.0 g/F50 ASTM D1709 Elmendorf Tear Strength (MD) 5.0 gF ASTM D1922 Elmendorf Tear Strength (TD) 50.0 gF ASTM D1922 Secant Modulus 1% (MD) 750.0 MPa ASTM D882 Secant Modulus 1% (TD) 870.0 MPa ASTM D882 Sealing Initial Temperature 125.0 °C Braskem Method - Note
Blown Film Properties:
- Film with 12,5 microns produce in a 75mm extruder with 1,3 mm of die gap and a blow‐up ra o of 4.5:1. (MD = extrusion direction and TD = transversal direction).